Liquid form ester/resin adhesion promoter

ABSTRACT

A rubber composition including a natural or synthetic rubber, and an adhesive resin capable of unexpected adhesion to metal, polymer and glass substrates, particularly cords in radical tires, hoses, conveyor belts, transmission belts, and the like by the addition of a liquid composition containing long chain esters, including mono, di- and tri-esters, and one or more reactive diluents. In the preferred embodiment, the reactive diluent is selected from (1) glycidyl ethers, (2) diglycidyl ethers; (3) aliphatic, straight chain epoxides; (4) epoxidized vegetable oils, particularly epoxidized soybean oil; (5) cycloaliphatic epoxies; (6) glycidyl esters, and (7) diglycidyl esters.

CROSS REFERENCE TO RELATED APPLICATIONS

[0001] This is a continuation-in part of U.S. patent application Ser. No. 10/434,616, filed on May 9, 2003, which is a continuation-in-part of U.S. patent application Ser. No. 10/301,770, filed Nov. 21, 2002, which is a continuation-in-part of U.S. patent application Ser. No. 10/144,229, filed May 10, 2002, the entire respective disclosures of which are hereby incorporated by reference.

FIELD OF THE INVENTION

[0002] The present invention is directed to adhesion promoters for adhering elastomers, including natural and/or synthetic rubbers, to natural or synthetic polymeric cord or fabric substrates, and/or metal cord or metal substrates, particularly cords in the manufacture of cord-reinforced rubber articles, such as tires, hoses, conveyor belts, transmission belts, and the like, and includes reactive diluents, in addition to the compositions described in the parent application.

BACKGROUND OF THE INVENTION

[0003] Many rubber articles, principally automobile tires, but also including hoses, conveyor belts, power train belts, e.g., transmission belts, and the like, are usually reinforced with fibrous or metal cords. In all such instances, the fiber must be firmly bonded to the rubber. This is so whether the fiber is a natural or synthetic polymer, or metallic, and whether the rubbers are natural or synthetic.

[0004] The conventional practice has been to prepare the fiber by pretreatment with a combination of hexaamethoxymelamine or hexamethylene-tetramine and phenol-formaldehyde condensation product, wherein the phenol is almost always resorcinol. By a mechanism not completely understood, the resin reacts with the fiber and the rubber, effecting a firm reinforcing bond.

[0005] One method for preparing rubber compositions reinforced with cords entails compounding a vulcanizing rubber stock composition with the components of an adhesive resin condensation product. The components of the condensation product include a methylene acceptor and a methylene donor. The most commonly employed methylene acceptor is a phenol, such as resorcinol, while the most commonly employed methylene donor is a melamine, such as N-(substituted oxymethyl)melamine. The effect achieved is resin formation in-situ during vulcanization of the rubber, creating, a bond between the metal or polymeric cords and the rubber, irrespective of whether the cords have been pretreated with an additional adhesive, such as a styrene-butadiene latex, polyepoxides with a blocked isocyanate, and the like.

[0006] Resorcinol-free vulcanizable rubber compositions are known. For example, U.S. Pat. No. 5,298,539 discloses vulcanizable rubber compositions containing uncured rubber, a vulcanizing agent and at least one additive selected from the group consisting of derivatives of melamine, acetoguanamine, benzoguanamine, cyclohexylguanamine and glycoluril monomer and oligomers of these monomers. These derivatives are substituted on average at two or more positions on the monomer or each unit of the oligomer with vinyl terminated radicals and the composition is free of resorcinol.

[0007] Another manner of eliminating resorcinol from vulcanizable rubber compositions has relied on the use of alternative coreactants. U.S. Pat. No. 4,038,220 describes a vulcanizable rubber composition which comprises a rubber, a filler material, N-(substituted oxymethyl)melamine and at least one of α- or β-naphthol. This reference employs the monohydric phenols, α- or β-naphthol, as methylene acceptors in the resin forming reaction during vulcanization in the absence of resorcinol. The use of resorcinol-formaldehyde resin to replace resorcinol in vulcanizable rubber compositions is also known. For example, see A. Peterson, et al., “Resorcinol Bonding Systems for Steel Cord Adhesion”, Rubber World (August 1984).

[0008] An increased need in the industry for fiber reinforcing of rubber to survive high dynamic stress, such as flexing, to avoid tire belt separation has brought about a continuing search for other and better methods for achieving high adhesive strength.

[0009] Tires typically have a construction such that a carcass, edge portions of a belt, an under-belt pad and the like are intricately combined with each other in its shoulder portion. The under-belt pad provided continuously along the circumferential shoulder portion of the tire between a tread rubber portion and the carcass and extending outwardly of the belt edge portions along the width of the tire is a thick rubber layer, which is a structural characteristic for alleviating a shear stress possibly generated between the belt edge portions and the carcass. Further, since the under-belt pad is repeatedly subjected to loads during running, heat is liable to build-up in the under-belt pad, thereby causing internal rubber destruction in the under-belt pad and adhesion failures between the rubber components and between a rubber portion and cords (steel cords) in the carcass. This causes separation of the belt edge portions and ply separation in the carcass resulting in breakdown of the tire. One conventional approach to this problem is that the under-belt pad is formed of a rubber compound which contains a reduced amount of carbon black for suppression of heat build-up.

[0010] However, the rubber compound for the under-belt pad is softened by the reduction of the carbon black content therein. This also results in the adhesion failure and the internal rubber destruction in the under-belt pad due to the heat build-up, thereby causing the ply separation and the belt separation in the tire during running. Therefore, this approach is not satisfactory in terms of the durability of the tire. The deterioration of the durability of the tire which results from the heat build-up attributable to the structural characteristic of the under-belt pad is a more critical problem, since the recent performance improvement of automobiles requires that tires have a higher durability under higher speed running and heavy loads.

[0011] Despite their good abrasion resistance, radial tires become unusable sooner than bias tires because of the belt separation which takes place while the tread still remains. One way that this problem has been addressed is by improving the tread or steel cord-embedding rubber. For example, an improved tread is of dual layer structure, with the inner layer (base tread adjacent to the belt) being made of a rubber composition which is saved from heat generation at the sacrifice of abrasion resistance, and the outer layer (cap tread) being made of a rubber composition of high abrasion resistance. Also, an improved steel cord-embedding rubber is made of a rubber composition containing an adhesive such as a cobalt salt of an organic acid, hydroxybenzoic acid, and resorcinol, which increases adhesion between rubber and steel cord. These improvements, however, are not completely successful.

[0012] Other adhesion promoters have been used in an attempt to avoid belt separation, for example, special latices such as, for example, a vinyl-pyridine latex (VP latex) which is a copolymer of about 70% butadiene, about 15% styrene and about 15% 2-vinylpyridine. Examples of other latices which are present in adhesion promoters are acrylonitrile rubber latices or styrene-butadiene rubber latices. These can be used as such or in combination with one another. Especially suitable adhesion promoters for polyesters are also those which are applied in multi-stage processes, for instance a blocked isocyanate being applied in combination with polyepoxide and the material then being treated using customary resorcinol-formaldehyde resins (RFL dip). It is also known to use combinations of RFL dips with other adhesion-promoting substances such as, for example, a reaction product of triallyl cyanurate, resorcinol and formaldehyde or p-chlorophenol, resorcinol and formaldehyde.

[0013] Not only is it necessary that adhesion between rubber and metal, e.g., steel or polymeric cord be high, but it is also necessary that a decrease in adhesion be as small as possible while tires are in use. In actuality, tires containing a steel cord-embedding rubber with good adhesion occasionally lose the initial adhesion to a great extent after use. The following are the possible reasons why adhesion between steel cord and rubber decreases while tires are in use:

[0014] (1) Tires are subject to many minute cuts when they run over gravel or sharp objects. The cuts reaching the inside of the tread permit air and moisture to infiltrate into the tire, promoting the aging and fatigue of the embedding rubber and also rusting the steel cord. All this leads to a decrease in adhesion.

[0015] (2) The adhesion improver incorporated into the steel cord-embedding rubber diffuses and migrates into the tread rubber during vulcanization or tire use. This leads to a decrease in adhesion.

[0016] (3) The softener and other additives incorporated into the tread migrate into the steel cord-embedding rubber. This also leads to a decrease in adhesion.

[0017] Despite the various proposals made to improve the adherence of cord to rubber in vulcanizable rubber compositions, there is a continuing need for commercially available cost effective additives that improve the adhesion of rubber to fibrous or metal cords in vulcanizable rubber compositions.

[0018] The adhesion promoter systems of the present invention far surpass any extant adhesion promoters known in the art for adhesion of metal and/or polymeric cord to vulcanizable rubber.

SUMMARY OF THE INVENTION

[0019] In brief, it has been found that the use of long chain esters formed by reacting mono, di-, and/or tri-carboxylic acids containing one, two, or three C₆-C₂₄ long chain radicals or fatty acid residues, and alcohols containing a C₃-C₂₄ alkyl group, in a natural or synthetic vulcanizable rubber, unexpectedly increases the adhesion between the rubber and a metal or polymeric substrate, such as metal or polymeric surfaces, particularly cords used in reinforcing rubber in tires, hoses, conveyor belts, motor mounts, automotive drive train belts, including transmission belts, and the like, when added with an adhesive resin, such as a melamine-containing resin or a phenol-, e.g., resorcinol-containing resin, e.g., a Novolak resin.

[0020] In accordance with the present invention, it has been found that the addition of one or more reactive organic solvents (diluents) to the rubber compositions described herein, in addition to a solvent used to solubilize the adhesive resin, or as a replacement for any portion, or all of, the resin solvent, unexpectedly increases the adhesion of the rubber composition to substrates such as polymeric cord, metal cord, polymeric fabric, and metal, particularly cords in the manufacture of cord-reinforced rubber articles, such as tires, hoses, conveyor belts, transmission belts, and the like.

[0021] Examples of the reactive diluents include (1) glycidyl ethers, (2) diglycidyl ethers; (3) aliphatic, straight chain epoxides; (4) epoxidized vegetable oils, particularly epoxidized soybean oil; (5) cycloaliphatic epoxies; (6) glycidyl esters, and (7) diglycidyl esters.

[0022] Examples of suitable substrates include steel, brass-coated steel, brass, polyester, Aramid, textiles, copper, glass, and the like. Application of the adhesive promoters of the invention is particularly contemplated with steel cord, brass-coated steel cord, brass cord, polyester fiber cord, Aramid fiber cord, glass cord, fabric and flat metal surfaces, and the like. While these resins have been used before to adhere metal tire cord to a vulcanizable rubber, and theoretically bond the rubber to the resin, surprisingly good adhesion has been found by additionally adding one or more long chain mono-, di-, and/or tri-esters, particularly dimerate esters reacted from C₁₈ fatty acids, and C₃-C₂₄ alcohols, preferably, C₃-C₁₈ alcohols, more preferably C₆-C₁₈ alcohols. Preferably, the esters provide unexpected, tenacious bonding between polymeric or metal cord and rubber, when combined with an adhesive resin. It is theorized that the long chain esters of the invention strongly adhere both to the rubber and to the resin, with the resin providing sufficient ionic bonding to the reinforcing cords.

[0023] One aspect of the composition and articles described herein is to provide a radial tire for heavy load vehicles characterized by good adhesion between steel or polymeric cord and steel cord-embedding rubber, said adhesions lasting for a long time with only a small loss of adhesion while tires are in use. Another aspect of the compositions and articles described herein is to provide a radial tire for vehicles and other cord-embedded rubber articles which are superior in cord adhesion to rubber.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0024] The adhesion promoter systems of the invention include at least one long chain ester compound and at least one adhesive resin. The adhesion promoter systems are useful for improving the adhesion of rubber to metal and polymeric substrates, particularly metal and polymeric cord. Surprisingly, the adhesion promoter systems disclosed herein significantly increase the adhesion of rubber compositions to such metal and polymeric substrates. In the description, the terms “adhesion promoter system” and “adhesion promoter” may be used interchangeably.

[0025] In the adhesion promoter systems of the invention, long chain esters are typically added to natural or synthetic rubber with a vulcanizing agent and an adhesive resin. The adhesion promoter systems may be added to a natural and/or synthetic rubber(s), as a neat liquid, in order to promote adhesion. Typically, however, the adhesion promoters are mixed with a dry carrier, such as calcium silicate, to form an alternative delivery system, which can be incorporated into natural and/or synthetic rubber(s). In such a method, the carrier facilitates delivery of the active adhesion promoting agents to the rubber(s). In yet another refinement of the invention, the adhesion promoter may be formulated as a “polymer masterbatch.” According to this aspect of the invention, a pellet comprising polymer (about 6 wt. % to about 20 wt. %), filler or inert ingredients (about 0 wt. % to about 14 wt. %), with the balance being an adhesion promoter system (i.e., at least one ester compound in accordance with formulas I-IV and at least one adhesive resin such as melamine) is added to a natural or synthetic rubber. Typically, the masterbatch polymer and the rubber to which the masterbatch polymer is added are miscible. Preferably, the masterbatch polymer and the rubber are the same.

[0026] Throughout the specification, the adhesion promoter systems are generally used in an amount between about 0.2% by weight and about 30% by weight. Typically, each component of an adhesion promoter system of the invention (i.e., an ester in accordance with formulas I-IV, and an adhesive resin) is present in an amount between about 0.1% and about 15% by weight, usually between about 1 wt. % and about 10 wt. %, and most preferably between about 2 wt. % and about 8 wt. %, based on the weight of natural and synthetic rubber in the composition. The reactive diluent is present in an amount of about 0.5% to about 50% by weight, based on the weight of the adhesion promoter system (ester of formulas I-IV plus adhesive resin). Usually, the reactive diluent is present in an amount of about 5% to about 40% by weight, most preferably about 10% to about 30% by weight, based on the total weight of adhesive resin plus ester of formulas I-IV.

[0027] Ranges may be expressed herein as from “about” or “approximately” one particular value and/or to “about” or “approximately” another particular value. When such a range is expressed, another embodiment includes from the one particular value and/or to the other particular value. Similarly, when values are expressed as approximations, by use of the antecedent “about,” it will be understood that the particular value forms another embodiment.

[0028] The long chain esters may be monoesters, diesters, triesters, or mixtures thereof, that may include saturated or unsaturated hydrocarbon chains, straight chain or branched having none, one, two or three double bonds in the hydrocarbon chains.

[0029] The monoesters have a formula I, as follows:

[0030] wherein R¹ is a C₃-C₂₄ alkyl, preferably C₃-C₁₈ alkyl, more preferably C₆-C₁₈ alkyl, straight chain or branched, saturated or unsaturated containing 1 to 3 carbon-to-carbon double bonds. R² is a C₃-C₂₄, preferably C₆-C₂₄, more preferably C₈-C₁₈ saturated hydrocarbon, or an unsaturated hydrocarbon having 1 to 6, preferably 1 to 3 carbon-to-carbon double bonds.

[0031] The diesters have a formula II or III, as follows:

[0032] wherein n=3-24, preferably 6-18, and more preferably 3-10, and R³ and R⁴, same or different, are C₃-C₂₄ alkyl, preferably C₃-C₁₈ alkyl, more preferably C₆-C₁₈ alkyl radicals, straight chain or branched, saturated or unsaturated containing 1 to 3 carbon-to-carbon double bonds.

[0033] wherein R⁵ and R⁷, same or different, are C₃-C₂₄ alkyl, preferably C₆-C₂₄ alkyl, more preferably C₈-C₁₈ alkyl, straight chain or branched, either saturated or containing 1 to 6, preferably 1 to 3, carbon-to-carbon double bonds;

[0034] R⁶ and R⁸, same or different, are C₃-C₂₄ alkyl, preferably C₃-C₁₈ alkyl, more preferably C₆-C₁₈ alkyl, straight chain or branched, saturated or unsaturated containing 1 to 3 carbon-to-carbon double bonds; and

[0035] R¹⁰ and R¹¹, same or different, are C₃-C₂₄ saturated hydrocarbon chains, preferably C₃-C₁₈, more preferably C₆-C₁₈, straight chain or branched; or unsaturated C₃-C₂₄ hydrocarbon chains, preferably C₃-C₁₈, more preferably C₆-C₁₈, straight chain or branched, containing 1 to 6, preferably 1 to 3, carbon-to-carbon double bonds.

[0036] The triesters have a formula IV, as follows:

[0037] wherein R¹², R¹⁴ and R¹⁸, same or different, are C₃-C₂₄ alkyl, preferably C₆-C₂₄ alkyl, more preferably C₈-C₁₈ alkyl, straight chain or branched, either saturated or containing 1 to 6, preferably 1 to 3, carbon-to-carbon double bonds;

[0038] R¹³, R¹⁵ and R¹⁹, same or different, are C₃-C₂₄ alkyl, preferably C₃-C₁₈ alkyl, more preferably C₆-C₁₈ alkyl, straight chain or branched, saturated or unsaturated containing 1 to 3 carbon-to-carbon double bonds; and

[0039] R¹⁶, R¹⁷ and R²⁰, same or different, are C₃-C₂₄ saturated hydrocarbon chains, preferably C₃-C₁₈, more preferably C₆-C₁₈, straight chain or branched; or unsaturated C₃-C₂₄ hydrocarbon chains, preferably C₃-C₁₈, more preferably C₆-C₁₈, straight chain or branched, containing 1 to 6, preferably 1 to 3, carbon-to-carbon double bonds.

[0040] The fatty acid residues or hydrocarbon chains R², R⁵, R⁷, R¹², R¹⁴ and R¹⁸ of the esters of formulas I, II, III, and IV can be any C₃-C₂₄, preferably C₆-C₂₄, more preferably C₈-C₁₈, hydrocarbon chain, either saturated or containing 1 to 6, preferably 1 to 3, carbon-to-carbon double bonds, derived from animal or vegetable fatty acids such as butter; lard; tallow; grease; herring; menhaden; pilchard; sardine; babassu; castor; coconut; corn; cottonseed; jojoba; linseed; oiticica; olive; palm; palm kernel; peanut; rapeseed; safflower; soya; sunflower; tall; and/or tung. Examples are the hydrocarbon chain residues from the following fatty acids, where the number in parentheses indicates the number of carbon atoms, and the number of double bonds, e.g., (C₂₄₋₆) indicates a hydrocarbon chain having 24 carbon atoms and 6 double bonds: Hexanoic (C₆₋₀); Octanoic (C₈₋₀); Decanoic (C₁₀₋₀); Dodecanoic (C₁₂₋₀); 9-Dodecenoic (CIS) (C₁₂₋₁); Tetradecanoic (C₁₄₋₀); 9-Tetradecenoic (CIS) (C₁₄₋₁); Hexadecanoic (CIS) (C₁₆₋₀); 9-Hexadecenoic (CIS) (C₁₆₋₁); Octadecanoic (C₁₈₋₀); 9-Octadecenoic (CIS) (C₁₈₋₁); 9-Octadecenoic, 12-Hydroxy-(CIS) (C₁₈₋₂); 9,12-Octadecadienoic (CIS, CIS) (C₁₈₋₂); 9, 12, 15 Octadecatrienoic (CIS, CIS, CIS) (C₁₈₋₃); 9,11,13 Octadecatrienoic (CIS, TRANS, TRANS) (C₁₈₋₃); 9,11,13 Octadecatrienoic, 4-Oxo (CIS, TRANS, TRANS) (C₁₈₋₃); Octadecatetrenoic (C₁₈₋₄); Eicosanoic (C₂₀); 11-Eicosenoic (CIS) (C₂₀₋₁); Eicosadienoic (C₂₀₋₂); Eicosatrienoic (C₂₀₋₃); 5,8,11,14 Eicosatetraenoic (C₂₀₋₄); Eicosapentaenoic (C₂₀₋₅); Docosanoic (C₂₂); 13 Docosenoic (CIS) (C₂₂₋₁); Docosatetraenoic (C₂₂₄); 4,8,12,15,19 Docosapentaenoic (C₂₂₋₅); Docosahexaenoic (C₂₂₋₆); Tetracosenoic (C₂₄₋₁); and 4, 8, 12, 15, 18, 21 Tetracosahexaenoic (C₂₄₋₆).

[0041] Examples of particularly useful diesters of formula II include a saturated diester formed by the reaction of sebacic acid and 2-ethylhexyl alcohol:

[0042] Other useful diesters falling within formula II include the saturated diester formed by the reaction of sebacic acid with tridecyl alcohol,

[0043] and the unsaturated diester formed by reaction of sebacic alcohol with oleyl alcohol:

[0044] Useful cyclic diesters falling within formula III include dimerate ester structures formed by the reaction of a C₃₆ dimer acid derived from tall oil fatty acids and C₃-C₂₄, preferably C₃-C₁₈, more preferably C₆-C₁₈ alcohol, straight chain or branched, saturated or unsaturated containing 1 to 3 carbon-to-carbon double bonds. Examples of such cyclic esters include the following structures, wherein the dimer acid corresponding to structure A is formed by self reaction of linoleic acid, the dimer acid corresponding to structure B is formed by reacting linoleic acid with oleic acid, and the dimer acid corresponding to structure C is formed by reacting linoleic acid with linolenic acid:

[0045] wherein each R, same or different, in formulas (A), (B), and (C) is a C₃-C₂₄ radical, preferably C₃-C₁₈, more preferably C6-C₁₈, straight chain or branched, saturated or unsaturated containing 1 to 3 carbon-to-carbon double bonds. RX-13804 is another example of an unsaturated diester (dimerate ester) formed by the reaction of a predominantly C₃₆ dimer acid reacted with 2-ethylhexyl alcohol. RX-13824 is an additional unsaturated diester (dimerate ester) formed by the reaction of a predominantly C₃₆ dimer acid with tridecyl alcohol.

[0046] A representative example of the triester (trimerate ester) of formula IV is the following structure (D);

[0047] wherein each R¹, R², and R³, same or different, is a C₃-C₂₄ radical, preferably C₃-C₁₈, more preferably C₆-C₁₈, straight chain, or branched, saturated or unsaturated containing 1 to 3 carbon-to-carbon double bonds.

[0048] A particularly useful blend of long chain esters is formed from blends of mono, dimer, and trimer acids, for example, products having CAS#: 61788-89-4. Esters prepared from such products are blends including, primarily, the above C₃₆ and C₅₄ dimerate and trimerate esters (A), (B), (C) and (D), shown in the above structures, that is predominantly (more than 50% by weight) the C₃₆ dimerate esters (A), (B) and (C).

[0049] Commercially available blends of useful polybasic acids that can be reacted with C₃-C₂₄, preferably C₃-C₁₈, more preferably C₆-C₁₈ alcohols, straight chain or branched, saturated or unsaturated containing 1 to 3 carbon-to-carbon double bonds to produce the dimerate and trimerate esters, as blends, include the following: EMPOL® 1010 Dimer Acid; EMPOL® 1014 Dimer Acid; EMPOL® 1016 Dimer Acid; EMPOL® 1018 Dimer Acid; EMPOL® 1022 Dimer Acid; EMPOL® 1024 Dimer Acid; EMPOL® 1040 Trimer Acid; EMPOL® 1041 Trimer Acid; EMPOL® 1052 Polybasic Acid; and similar PRIPOL™ products from Uniqema as well as UNIDYME® products from Arizona Chemical.

[0050] Particularly useful long chain ester additives are made by reacting any of the long chain mono, dimer and/or trimer acids with one or more straight chain or branched C₃-C₂₄, preferably C₃-C₁₈, more preferably C₆-C₁₈ alcohols to produce the esters of formulas I, II, III and IV. The above dimer, trimer, and polybasic acids are produced by dimerizing, trimerizing, and polymerizing (oligomerizing) long chain carboxylic acids from the above-mentioned fatty acids. The fatty acids may be mixtures. Accordingly, the dimer acid produced by dimerizing a C₁₈ carboxylic acid (typically, a mixture of stearic, oleic, linoleic, and linolenic), after esterification, will result in a blend of numerous dimerate and trimerate esters in accordance with formulas III and IV, including saturated and unsaturated esters (i.e., some long chain esters may contain hydrocarbon chains having 1 to 6, generally 1 to 3, carbon-to-carbon double bonds). Any one, or any blend, of the esters of formulas I, II, III and/or IV, when combined with an adhesive resin, will function to increase the adhesion of natural or synthetic rubber to metal or polymeric cord, metal or polymeric substrates, such as polymeric woven or non-woven fabrics, and metal flat stock materials.

[0051] The adhesion promoters include an adhesive resin, which preferably is a condensation product of a formaldehyde or methylene donor and a formaldehyde or methylene acceptor, either pre-condensed, or condensed in-situ while in contact with the rubber. The term “methylene donor” is intended to mean a compound capable of reacting with a methylene acceptor (such as resorcinol or its equivalent containing a reactive hydroxyl group) and generate the resin outside of the rubber composition, or in-situ. Preferably, the components of the condensation product include a methylene acceptor and a methylene donor. The most commonly employed methylene acceptor is a phenol, such as resorcinol, while the most commonly employed methylene donor is a melamine, such as N-(substituted oxymethyl)melamine. The effect achieved is resin formation in-situ during vulcanization of the rubber, creating a bond between the metal or polymeric cords and the rubber, irrespective of whether the cords have been pretreated with an additional adhesive, such as a styrene-butadiene latex, polyepoxides with a blocked isocyanate, and the like. The long chain ester additive/resin combinations described herein are particularly useful with steel cord, where adhesive pretreatment has been largely ineffective.

[0052] Examples of methylene donors which are suitable for use in the rubber compositions disclosed herein include melamine, hexamethylenetetramine, hexaethoxymethylmelamine, hexamethoxymethylmelamine, lauryloxymethyl-pyridinium chloride, ethoxy-methylpyridinium chloride, trioxan hexamethoxy-methylmelamine, the hydroxy groups of which may be esterified or partly esterified, and polymers of formaldehyde, such as paraformaldehyde. In addition, the methylene donors may be N-substituted oxymethylmelamines, of the general formula:

[0053] wherein X is an alkyl having from 1 to 8 carbon atoms R³, R⁴, R⁵, R⁶ and R⁷ are individually selected from the group consisting of hydrogen, an alkyl having from 1 to 8 carbon atoms and the group —CH₂OX. Specific methylene donors include hexakis(methoxymethyl)melamine; N,N′,N″trimethyl/N,N′,N″-trimethylol-melamine; hexamethylolmelamine; N,N′,N″-dimethylolmelamine; N-methylol-melamine; NN′-dimethylolmelamine; N,N′,N″-tris(methoxymethyl)melamine; and N,N′,N″-tributyl-N,N′,N″-trimethylol-melamine. The N-methylol derivatives of melamine are prepared by known methods.

[0054] The amount of methylene donor and methylene acceptor, pre-condensed or condensed in-situ, that are present in the rubber composition may vary. Typically, the amount of pre-condensed methylene donor and methylene acceptor is present will range from about 0.1% to about 15.0%; or each can be added separately in an amount of about 0.1% to about 10.0%, based on the weight of natural and/or synthetic rubber in the composition. Preferably, the amount of each of a methylene donor and methylene acceptor added for in-situ condensation ranges from about 2.0% to about 5.0%, based on the weight of natural and/or synthetic rubber in the composition. The weight ratio of methylene donor to the methylene acceptor may vary. Generally speaking, the weight ratio will range from about 1:10 to about 10:1. Preferably, the weight ratio ranges from about 1:3 to 3:1.

[0055] Resorcinol-free vulcanizable rubber compositions also are useful in the rubber compositions described herein. For example, resorcinol-free adhesive resins and adhesive compounds useful in the adhesion promoter systems (i.e., when combined with the long chain esters described herein) include those described in U.S. Pat. Nos. 5,891,938 and 5,298,539, both hereby incorporated by reference. The '938 patent discloses vulcanizable rubber compositions containing an uncured rubber and a self-condensing alkylated triazine resin having high imino and/or methylol functionality. U.S. Pat. No. 5,298,539 discloses rubber additives which are substituted derivatives based on cyclic nitrogen compounds such as melamine, acetoguanamine, cyclohexylguanamine, benzoguanamine, and similar alkyl, aryl or aralkyl substituted melamines, glycoluril and oligomers of these compounds. In particular, the adhesive resins and adhesive compounds which are useful as the adhesive resins in the rubber compositions described herein include the following: adhesive resins selected from the group consisting of derivatives of melamine, acetoguanamine, benzoguanamine, cyclohexylguanamine and glycoluril monomers and oligomers of these monomers, which have been substituted on average at two or more positions on the monomer or on each unit of the oligomer with vinyl terminated radicals, the vulcanizable rubber composition being free of resorcinol; and, these derivatives which have been further substituted on average at one or more positions with a radical which comprises carbamylmethyl or amidomethyl.

[0056] Further, the adhesive resin can be any of the compounds of the following formulas:

[0057] and positional isomers thereof,

[0058] wherein, in each monomer and in each polymerized unit of the oligomers, Y is selected from methyl, phenyl and cyclohexyl, and, on average,

[0059] at least two R are —CH₂—R¹,

[0060] and any remaining R and H, and

[0061] at least 2 R¹ are radicals selected from:

[0062] CH₂═C(R²)—C(O)—O—,

[0063] CH₂═C(R²)C(O)-Z,

[0064] CH₂═C(R²)—C(O)—NH—, and

[0065] CH₂═C(R²)—CH₂—O—,

[0066] wherein R² is hydrogen or C₁-C₁₈ alkyl, and Z is a radical selected from:

[0067] —O—CH₂—CH₂—O—,

[0068] —O—CH₂—CH(CH₃)—O—,

[0069] —O—CH₂—CH₂—CH₂O—, and

[0070] —O—CH(C₂H₅)—O—, and

[0071] any remaining R¹ radicals are selected from

[0072] —O—R³,

[0073] —NH—C(O)—OR⁴, and

[0074] —NH—C(O)—R⁴, and

[0075] wherein R₃ is hydrogen or R₄, and

[0076] R₄ is a C₁-C₁₈ alkyl, alicyclic, hydroxyalkyl, alkoxyalkyl or aromatic radical, and in the oligomers,

[0077] P is 2 to about 10, and

[0078] L is methylene or the radical

[0079] —CH₂—O—CH₂—.

[0080] These adhesive compounds are particularly useful, wherein on average at least one R¹ in each monomer or in each oligomerized unit is —NH—C(O)OR⁴,

[0081] particularly the compounds of the following formulas:

[0082] Particularly useful adhesive resins include the above formulas wherein on average, at least one R radical in each monomer or in each oligomerized unit is

[0083] —CH₂—NH—C(O)—OR⁴,

[0084] wherein R⁴ is a C₁-C₁₈ alkyl, alicyclic, hydroxyalkyl, alkoxyalkyl or aromatic radical, and

[0085] wherein, on average, at least two R radicals are selected from

[0086] CH₂═C(CH₃)C(O)O—C₃H₆—O—CH₂—and

[0087] CH₂═CH₂—C(O)O—C₂H₄—CH₂— and

[0088] at least one R radical is selected from

[0089] —CH₂—NH—C(O)—O—CH₃, and

[0090] —CH₂—NH—C(O)—O—C₃H₇.

[0091] These adhesive resins and compounds can include additional additives, particularly those selected from hydroxymethylated and alkoxymethylated (alkoxy having 1-5 carbon atoms) derivatives of melamine, acetoguanamine, benzoguanamine, cyclohexylguanamine and glycoluril and their oligomers.

[0092] Additional adhesive resins useful in the rubber compositions described herein include self-condensing alkylated triazine resins selected from the group consisting of (i), (ii), and (iii):

[0093] (i) a self-condensing alkylated triazine resin having at least one of imino or methylol functionality and represented by the formula (I)

[0094] (ii) an oligomer of (i), or

[0095] (iii) a mixture of (i) and (ii), wherein

[0096] Z is —N(R)(CH₂OR¹), aryl having 6 to 10 carbon atoms, alkyl having 1 to 20 carbon atoms or an acetyl group,

[0097] each R is independently hydrogen or —CH₂OR¹, and

[0098] each R¹ is independently hydrogen or an alkyl group having 1 to 12 carbon atoms,

[0099] provided that at least one R is hydrogen or —CH₂OH and at least one R¹ is selected from the alkyl group; and

[0100] wherein the vulcanizable rubber composition is substantially free of methylene acceptor coreactants.

[0101] These adhesive resins are particularly useful wherein at least one R group is hydrogen and/or wherein at least one R¹ group is a lower alkyl group having 1 to 6 carbon atoms, particularly where the adhesive resin is a derivative of melamine, benzoguanamine, cyclohexylguanamine, or acetoguanamine, or an oligomer thereof.

[0102] One particularly useful alkylated triazine adhesive resin of the above formula is wherein Z is —N(R)(CH₂OR¹).

[0103] Another manner of eliminating resorcinol in an adhesive resin for rubber compositions, also useful herein, is N-(substituted oxymethyl)melamine and at least one of α- or β-naphthol. This adhesive resin employs the monohydric phenols, α- or β-naphthol, as methylene acceptors in the resin forming reaction during vulcanization in the absence of resorcinol.

[0104] Other adhesive resins useful in the rubber compositions described herein include special latices such as, for example, a vinyl-pyridine latex (VP latex) which is a copolymer of about 70% butadiene, about 15% styrene and about 15% 2-vinylpyridine; acrylonitrile rubber latices; and styrene-butadiene rubber latices. These can be used as such or in combination with one another. Another suitable adhesive resin useful herein, particularly for polyesters, are those which are applied in multi-stage processes, for instance a blocked isocyanate being applied in combination with polyepoxide and the material then being treated using customary resorcinol-formaldehyde resins (RFL dip). Additional useful adhesive resins include combinations of RFL dips with other adhesion-promoting substances such as, for example, a reaction product of triallyl cyanurate, resorcinol and formaldehyde or p-chlorophenol, resorcinol and formaldehyde.

[0105] Other suitable adhesive resins for use in the rubber and adhesion promoters described herein include polyurethane resins, epoxy resins, phenol aldehyde resins, polyhydric phenol aldehyde resins, phenol furfural resins, xylene aldehyde resins, urea formaldehyde resins, melamine formaldehyde resins, alkyd resins, polyester resins, and the like.

[0106] Typically, in the adhesion promoter systems, at least one ester compound in accordance with formulas I-IV is combined with an adhesive resin in a weight ratio between about 10 parts ester to about 1 part adhesive resin (i.e., a ratio of about 10:1, ester to resin, respectively) and about 1 part ester to about 10 parts resin (i.e., a ratio of about 1:10, ester to resin, respectively). More preferably, the esters are combined with an adhesive resin in a weight ratio between about 4 parts ester to about 1 part adhesive resin and about 1 part ester to about 4 parts resin. Most preferably, the ratio of ester to adhesive resin is approximately one to one in the adhesion promoter systems of the invention.

[0107] The adhesion promoters described herein also include one or more reactive diluents in an amount of about 0.1% to about 15% by weight based on the total weight of the adhesive resin and ester compound in the composition. To achieve the full advantage of the adhesion promoters described herein, the reactive diluent(s) are selected from (1) glycidyl ethers, (2) diglycidyl ethers; (3) aliphatic, straight chain epoxides; (4) epoxidized vegetable oils, particularly epoxidized soybean oil; (5) cycloaliphatic epoxies; (6) glycidyl esters, and (7) diglycidyl esters.

[0108] These reactive diluents function as solvents to compatibilize the rubber, adhesive resin, and long chain ester compositions described herein and are believed to participate chemically in the adhesion of the rubber composition to the substrates described herein.

[0109] The initial work with the long chain esters involved testing the esters in industrial rubber belts containing polyester cords for automotive power train systems. An important part of the construction of automotive belts is the bonding of the rubber to polyester cord. Polyester cord is used to provide strength and longevity to the belts. The polymer of choice for automotive belts is ethylene/propylene/diene polymer (EPDM). This polymer is excellent for the end use, but one of its drawbacks is poor adhesion to many substrates, such as polyester cord. Rubber companies go to great lengths to insure the proper adhesion between the EPDM and the polyester cord. At present, they use a treated cord that has a resorcinol-formaldehyde resin coating, and the resin-coated cords are then dipped in an adhesive. The resin-treated, adhesive coated cord is then bonded to the EPDM during the curing process. This is a time-consuming and expensive method to achieve rubber-to-polyester cord adhesion. The adhesion promoter systems of the invention advantageously improve adhesion of polyester cord to EPDM.

[0110] Other examples of substrates which are contemplated for use in the inventive compositions and methods include metal and polymeric layers, films, sheets, fibers, yams and/or fabrics, including textiles, polyesters, and Aramid fibers. Metals for use in the invention include steel, brass-coated steel, brass, aluminum, and copper. Adhesion to glass substrates can also be improved. Application of the adhesion promoters of the invention is particularly contemplated with steel cord, brass-coated steel cord, brass cord, polyester fiber cord, Aramid fiber cord, glass cord, fabric and flat metal surfaces, and the like. In the present application the term polymeric “cord” or “cords” is intended to include reinforcing elements used in rubber products including fibers, continuous filaments, staple, tow, yarns, fabric and the like, particularly cords for use in building the carcasses of tires such as truck tires.

[0111] The polymeric reinforcing element or cord comprises a plurality of substantially continuous fibers or monofilaments, including glass compositions, polyesters, polyamides and a number of other materials, useful in making the fibers for the reinforcing element or cords for polymeric rubber compositions and products are well known in the art. One of the preferred glasses to use is a glass known as E glass and described in “Mechanics of Pneumatic Tires,” Clark, National Bureau of Standards Monograph 122, U.S. Dept. of Commerce, issued November 1971, pages 241-243, 290 and 291, incorporated herein by reference. The number of filaments or fibers employed in the fiber reinforcing element or cord can vary considerably depending on the ultimate use or service requirements. Likewise, the number of strands of fibers used to make a fiber reinforcing element or cord can vary widely. In general, the number of filaments in the fiber reinforcing element or cord for a passenger car tire can vary from about 500 to 3,000 and the number of strands in the reinforcing element can vary from 1 to 10. Preferably the number of strands is from 1 to 7 and the total number of filaments about 2,000. A representative industry glass tire cord known as G-75 (or G-75, 5/0) has 5 strands each with 408 glass filaments. Another representative cord known as G-15 has a single strand containing 2,040 glass filaments.

[0112] The adhesive promoters of the invention can be used in numerous applications, including bonding the steel braid to the natural and/or synthetic rubber material of hoses and the metal housing of motor mounts.

[0113] The term “vulcanization” used herein means the introduction of three dimensional cross-linked structures between rubber molecules. Thus, thiuram vulcanization, peroxide vulcanization, quinoid vulcanization, resin vulcanization, metal salt vulcanization, metal oxide vulcanization, polyamine vulcanization, radiation vulcanization, hexamethylenetetramine vulcanization, urethane cross-linker vulcanization and the like are included in addition to sulfur vulcanization which is usual and most important.

[0114] Rubbers useful in the compositions described herein can be natural rubbers (NR) and/or synthetic rubbers.

[0115] Synthetic rubbers include homopolymers of conjugated diene compounds, such as isoprene, butadiene, chloroprene and the like, for example, polyisoprene rubber (IR), polybutadiene rubber (BR), polychloroprene rubber and the like; copolymers of the above described conjugated diene compounds with vinyl compounds, such as styrene, acrylonitrile, vinyl pyridine, acrylic acid, methacrylic acid, alkyl acrylates, alkyl methacrylates and the like, for example, styrene-butadiene copolymeric rubber (SBR), vinylpyridine-butadiene-styrene copolymeric rubber, acrylonitrile-butadiene copolymeric rubber, acrylic acid-butadiene copolymeric rubber, methacrylic acid-butadiene copolymeric rubber, methyl acrylate-butadiene copolymeric rubber, methyl methacrylate-butadiene copolymeric rubber, acrylonitrile-butadiene-styrene terpolymer, and the like; copolymers of olefins, such as ethylene, propylene, isobutylene and the like with dienes, for example isobutylene-isoprene copolymeric rubber (IIR); copolymers of olefins with non-conjugated dienes (EPDM), for example, ethylene-propylene-cyclopentadiene terpolymer, ethylene-propylene-5-ethylidene-2-norbornene terpolymer and ethylene-propylene-1,4-hexadiene terpolymer; polyalkenamer obtained by ring opening polymerization of cycloolefins, for example, polypentenamer; rubbers obtained by ring opening polymerization of oxirane ring, for example, polyepichlorohydrin rubber and polypropylene oxide rubber which can be vulcanized with sulfur, silicone rubbers, and the like. Furthermore, halides of the above-described various rubbers, for example, chlorinated isobutylene-isoprene copolymeric rubber (CI-IIR), brominated isobutylene-isoprene copolymeric rubber (Br-IIR), fluorinated polyethylene, and the like are included.

[0116] Particularly, the compositions described herein are characterized in that the surfaces of the vulcanized rubbers of natural rubber (NR), and synthetic rubbers, e.g. styrene-butadiene copolymeric rubber (SBR), polybutadiene rubber (BR), polyisoprene rubber (IR), isobutylene-isoprene, copolymeric rubber, halides of these rubbers (CI-IIR, Br-IIR) and copolymers (EPDM) of olefins with non-conjugated dienes, which are poor in the adhering ability, are improved to provide them a high adhering ability. Of course, the present invention can be applied to the other rubbers. All these rubbers may be kneaded with compounding agents conventionally used for compounding with rubber, for example, fillers, such as carbon black, silica, calcium carbonate, lignin and the like, softening agents, such as mineral oils, vegetable oils, prior to the vulcanization and then vulcanized.

[0117] The vulcanized rubbers, the surface of which has been treated with the adhesion promoter systems described herein can be easily adhered to the other materials, together with an adhesive resin, particularly metals and polymers, particularly in cord form.

[0118] In order to cure a rubber composition a vulcanizing agent such as a sulfur or peroxide vulcanizing agent is dispersed throughout the composition. The vulcanizing agent may be used in an amount ranging from 0.5 to 6.0%, based on the weight of the natural and/or synthetic rubbers in the composition, with a range of from 1.0 to 4.0% being preferred. Representative examples of sulfur vulcanizing agents include elemental sulfur (S₈), an amine disulfide, polymeric polysulfide and sulfur olefin adducts. Preferably, the sulfur vulcanizing agent is elemental sulfur.

[0119] Other suitable vulcanizing agents include thiuram, quinoid, metal salt, metal oxide, polyamine, vulcanization, radiation, hexamethylenetetramine, urethane cross-linker, and the like. Typical examples of peroxide vulcanizing agents include dibenzoyl peroxide and di(tertiary-butyl)peroxide.

[0120] The commonly employed carbon blacks used in conventional rubber compounding applications can be used as the carbon black in this invention. Representative examples of such carbon blacks include N110, N121, N220, N231, N234, N242, N293, N299, S315, N326, N330, M332, N339, N343, N347, N351, N358 and N375.

[0121] The rubber compositions described herein are compounded by methods generally known in the rubber compounding art, such as mixing the various sulfur-vulcanizable or peroxide-vulcanizable constituent rubbers with various commonly used additive materials such as, for example, sulfur donors, curing aids, such as activators and retarders and processing additives, such as oils, resins including tackifying resins and plasticizers, fillers, pigments, fatty acid, zinc oxide, waxes, antioxidants and antiozonants, retarders and peptizing agents. As known to those skilled in the art, the additives mentioned above are selected and commonly used in conventional amounts for tire tread applications. Typical amount of adhesive resins, comprise about 0.2 to about 10%, based on the weight of natural and/or synthetic rubbers, usually about 1 to 5%.

[0122] Typical amounts of zinc oxide comprise about 2 to about 5%. Typical amounts of waxes comprise about 1 to about 5% based on the weight of natural and/or synthetic rubbers. Often microcrystalline waxes are used. Typical amounts of retarders range from 0.05 to 2%. Typical amounts of peptizers comprise about 0.1 to 1%. Typical peptizers may be, for example, pentachlorothiophenol and dibenzamidodiphenyl disulfide. All additive percentages are based on the weight of natural and/or synthetic rubbers.

[0123] Accelerators may be used to control the time and/or temperature required for vulcanization and to improve the properties of the vulcanizate. The accelerator(s) may be used in total amounts ranging from about 0.5 to about 4%, preferably about 0.8 to about 1.5%, based on the weight of natural and/or synthetic rubbers. Suitable types of accelerators that may be used are amines, disulfides, guanidines, thioureas, thiazoles, thiurams, sulfenamides, dithiocarbamates and xanthates. If included in the rubber composition, the primary accelerator preferably is a sulfenamide. If a second accelerator is used, the secondary accelerator is preferably a guanidine, dithiocarbamate or thiuram compound.

[0124] When the adhesion promoter systems containing a long chain ester and an adhesive resin are used as a wire coat or bead coat, e.g., for use in a tire, the adhesion promoter system typically does not include an organo-cobalt compound, and may be used in whole or as a partial replacement for an organo-cobalt compound which serves as a wire adhesion promoter. When used in part, any of the organo-cobalt compounds known in the art to promote the adhesion of rubber to metal also may be included. Thus, suitable organo-cobalt compounds which may be employed, in combination with the non-cobalt adhesion promoter systems containing long chain esters described herein, include cobalt salts of fatty acids such as stearic, palmitic, oleic, linoleic and the like; cobalt salts of aliphatic or alicyclic carboxylic acids having from 6 to 30 carbon atoms; cobalt chloride, cobalt naphthenate; cobalt carboxylate and an organo-cobalt-boron complex commercially available under the designation Comend A from Shepherd Chemical Company, Cincinnati, Ohio.

[0125] Comend A is believed to have the structure:

[0126] wherein each R, same or different, is an alkyl group having from 9 to 12 carbon atoms, and B is a hydrocarbon chain, C₄-C₂₄, straight chain or branched, saturated or unsaturated.

[0127] Amounts of organo-cobalt compound which may be employed depend upon the specific nature of the organo-cobalt compound selected, particularly the amount of cobalt metal present in the compound. Since the amount of cobalt metal varies considerably in organo-cobalt compounds which are suitable for use, it is most appropriate and convenient to base the amount of the organo-cobalt compound utilized on the amount of cobalt metal desired in the finished composition. Accordingly, it may in general be stated that if an organo-cobalt compound is included in the rubber composition, the amount of organo-cobalt compound present in the stock composition should be sufficient to provide from about 0.01 percent to about 0.35 percent by weight of cobalt metal based upon total weight of the rubber in the composition, with the preferred amounts being from about 0.03 percent to about 0.2 percent by weight of cobalt metal based on the total weight of rubber in the composition.

[0128] The adhesion promoters described herein are especially effective in compositions in which the rubber is cis-polyisoprene, either natural or synthetic, and in blends containing at least 25% by weight of cis-polyisoprene with other rubbers. Preferably the rubber, if a blend, contains at least 40% and more preferably at least 60% by weight of cis-polyisoprene. Examples of other rubbers which may be blended with cis-polyisoprene include poly-1,3-butadiene, copolymers of 1,3-butadiene with other monomers, for example styrene, acrylonitrile, isobutylene and methyl methacrylate, ethylene/propylene/diene terpolymers, and halogen-containing rubbers such as chlorobutyl, bromobutyl and chloroprene rubbers.

[0129] The amount of sulphur in the composition is typically from 2 to 8 parts, for example from 3 to 6, by weight per 100 parts by weight of rubber, but lesser or larger amounts, for example from 1 to 7 or 8 parts on the same basis, may be employed. A preferred range is from 2.5 to 6 parts per 100 parts by weight of rubber.

[0130] Additional examples of vulcanization accelerators which can be used in the rubber compositions described herein are the thiazole-based accelerators, for example 2-mercaptobenzothiazole, bis(2-benzothiazolyl)disulphide, 2(2′,4′-dinitrophenyl-thio)benzothiazole, benzothiazole-2-sulphenamides for instance N-isopropylbenzothiazole-2-sulphenamide, N-tert-butyl-benzothiazole-2-sulphenamide, N-cyclohexylbenzo-thiazole-2-sulphenamide, and 2(morpholinothio)benzothiazole, and thiocarbamylsulphenamides, for example N,N-dimethyl-N′,N′-dicyclohexylthiocarbamoyl-sulphenamide and N(morpholinothiocarbonylthio)-morpholine. A single accelerator or a mixture of accelerators may be used. In the compositions described herein, these vulcanization accelerators are usually used in amounts of from 0.3 to 2, for example from 0.3 to 1.5, preferably from 0.4 to 1.0 and more preferably from 0.5 to 0.8, parts by weight per 100 parts by weight of rubber.

[0131] The adhesion promoters described herein are very effective in promoting bonding between rubber and brass, for example the bonding between rubber and brass-coated steel. The brass typically has a copper content of from 60 to 70% by weight, more especially from 63 to 68% by weight, with the optimum percentage depending on the particular conditions under which the bond is formed. The brass coating on brass-coated steel can have a thickness of, for example, from 0.05 to 1 micrometer, preferably from 0.07 to 0.7 micrometer, for example from 0.15 to 0.4 micrometer.

[0132] The long chain ester additive/resin combinations (i.e., adhesion promoter systems) described herein are particularly useful to adhere rubber to steel cord, where conventional adhesive pretreatment has been largely ineffective. Rubber can also be bonded effectively to alloys of cooper and zinc containing small amounts of one or more other metals, for example cobalt, nickel or iron.

[0133] For bonding rubber to zinc, as for example in bonding rubber to zinc-coated steel cords (which are widely used in the manufacture of conveyor belting) cobalt compounds have been used as adhesion promoters. Examples of such compounds are cobalt naphthenate and the cobalt-boron complexes described in GB 2 022 089 A.

[0134] Vulcanization of the rubber composition described herein is generally carried out at conventional temperatures ranging from about 100° C. to 200° C. Preferably, the vulcanization is conducted at temperatures ranging from about 110° C. to 180° C. Any of the usual vulcanization processes may be used such as heating in a press or mold, heating with superheated steam or hot air or in a salt bath.

[0135] Upon vulcanization of the rubber composition at a temperature ranging from 100° C. to 200° C., the rubber composition can be used for various purposes. For example, the vulcanized rubber composition may be in the form of a tire, belt, hose, motor mounts, gaskets and air springs. In the case of a tire, it can be used for various tire components. Such tires can be built, shaped, molded and cured by various methods which are known and will be readily apparent to those having skill in such art. When the rubber composition is used in a tire, its use may be in a wire coat, bead coat, tread, apex, sidewall and combination thereof. As can be appreciated, the tire may be a passenger tire, aircraft tire, truck tire, and the like. Preferably, the tire is a passenger tire. The tire may also be a radial or bias, with a radial tire being preferred.

[0136] The invention may be better understood by reference to the following examples in which parts and percentages are by weight unless otherwise indicated.

[0137] In Part I of this project, compounds were mixed into existing EPDM recipes and tested for adhesion. The following varieties were tested: Variable Example 1 Example 2 Example 3 Example 4 Example 5 Cyrez ® Cyrez ® Control- Cyrez ® Cyrez ® CRA- CRA- Current CRA- CRA- 133M 148M EPDM 133M/ 148M/ Formula RX-13804 RX-13804

[0138] The melamine-formaldehyde resins are known as adhesion promoters in the tire industry. The need for rubber-to-cord adhesion generally requires the presence of a methylene donor/methylene acceptor resin system, as described above. The typical system consists of hexakismethoxymethylmelamine (HMMM) as the donor and a Novolak resin (such as resorcinol) as the acceptor.

Results

[0139] The table below shows adhesion results with polyester cord in Examples 1-5. Adhesion-lbs-force Compound Variable Room Temperature 257° C. Example 1: 23.48 2.91 (Cyrez ® CRA-133M) Example 2: 21.57 3.58 (Cyrez ® CRA-148M) Example 3: 22.21 4.88 (Control) Example 4: 48.76 10.21 (Cyrez ® CRA-133M/ RX-13804) Example 5: 47.70 14.21 (Cyrez ® CRA-148M/ RX-13804)

[0140] The control (Example 3) was EPDM with the polyester cord pretreated with a melamine formaldehyde resin and an adhesive from Lord Corporation (Cary, N.C.). The polyester cord used in Examples 1, 2, 4, and 5 were treated with melamine formaldehyde resin but not with an adhesive. Examples 1 and 2 contain just the melamine resin and provide basically equal adhesion to the control compound, which is significant since the cords used were not coated with adhesive. Examples 4 and 5 contain a combination of resin and the esters described herein, and show an unexpected increase in adhesion. The adhesive forces for Examples 4 and 5 are increased at least 100% compared to the control and resin only Examples (1-3).

[0141] These results indicate that the resin/ester combination provides a dramatic increase in adhesive force between EPDM and polyester cord compared to the control compound and the compounds containing only resin.

[0142] The formulation and data collected for Examples 1-5 are shown in Table I: TABLE I Example 1 Example 2 Example 3 Example 4 Example 5 Nordel IP3720 (EPDM) 100.00 ————————————————————

N762 Carbon Black 56.00 ————————————————————

Kadox 930 Zinc Oxide 5.00 ————————————————————

Ricon 150 5.00 ————————————————————

Sartomer ST350 4.00 ————————————————————

Cyrez ® CRA-133M 7.00 — — 7.00 — Cyrez ® CRA-148M — 7.00 — — 7.00 RX-13804 — — — 10.00 10.00 Subtotal 177.00 177.00 170.00 187.00 187.00 Mill Addition Vulcup 40KE 7.00 ————————————————————

Total 184.00 184.00 170.00 194.00 194.0 Major Variable Cyrez ® Cyrez ® Cyrez ® Cyrez ® CRA-133M/ CRA-148M/ CRA-133M CRA-148M CONTROL RX-13804 RX-13804 Viscosity and Curing Properties Example 1 Example 2 Example 3 Example 4 Example 5 Mooney Viscosity at 212° F. Minimum Viscosity 41.3 41.9 41.8 30.3 33.9 t5, minutes 56.8 Mooney Viscosity at 250° F. Minumum Viscosity 31 32.7 34.9 25.9 28.5 t5, minutes 10.8 11.1 9.7 8.3 8.3 t10, minutes 11.8 12.8 11.3 9.3 9 t35, minutes 13.8 18.3 17 11.8 Oscillating Disc Rheometer at 350° F. M_(L) 19 9 8.3 6.3 8.8 M_(H) 151.9 159.3 156.6 57.8 62.9 t_(s)2, minutes 0.92 0.92 0.83 0.92 1.2 t′c(90), minutes 7.5 7.2 7.9 5.7 6.3 1.25 * t′c(90), minutes 9.4 9 9.9 7.1 7.8 Cure Rate Index 15.2 16 14.1 21.1 19.7 Original Physical Properties Stress @ 100% Elongation, MPa 13.1 14.1 15.2 4.7 4.9 psi 1905 2050 2200 680 705 Stress @ 200% Elongation, MPa 9.9 9.5 Stress @ 300% Elongation, MPa Tensile Ultimate, MPa 19.0 18.1 18.7 12.5 10.9 psi 2760 2625 2705 1815 1580 Elongation @ Break, % 135 120 115 250 235 Hardness Duro A, pts. 83 83 80 78 75 Specific Gravity 1.1043 1.1085 1.1061 1.1075 1.1081

Adhesion Promoter Part II

[0143] Based on Part I results which show improved adhesion of EPDM rubber to polyester cord, the resin/ester combination was evaluated in a standard natural rubber compound used for metal cord adhesion.

[0144] The compounds tested in this study were varied in ester content, with resin content kept constant. The following Table II lists the adhesion results for original, air oven aging, and humidity aging, in Examples 6-12, with parts by weight of resin and ester set forth in parentheses. TABLE II Recipe Variable Standard Cyrez CRA-148 Resorcinol M(8)/SM (3.85)/melamine Cyrez CRA- Cyrez CRA- Cyrez CRA- Cyrez CRA- RX-13804(6)/ formaldehyde Cyrez CRA- 148M(8)/SM 148M(8)/SM 148M(8)/SM 148M(8)/SM Sulfur(8.4)/Vulkacit (4.23) 148M RX-13804(8) RX-13804(6) RX-13804(4) RX-13804(2) (0.75) Example 6 Example 7 Example 8 Example 9 Example 10 Example 11 Example 12 Adhesion to Steel Cord Original Properties: Max. Force, lbs. (avg.) Average 176.2 156 162.7 162.6 138.6 167.4 162 Coverage, % 100 95 100 100 100 99 100 Air Oven Aging: 48 hrs @ 121° C. (250° F.) Max. Force, lbs.(avg.) Average 105.6 73.5 68.9 70.8 77.6 87.7 123 Coverage, % 99 93 97 97 99 95 95 Force Change, % −40 −53 −58 −57 −44 −48 −24 Adhesion to Steel Cord Humidity Aging: 7 Days @ 94° C. (200° F.) Max. Force, lbs. (avg.) Average 152.3 119.7 130.4 160.3 137.7 136.9 152.7 Coverage, % 100 98 100 100 100 100 99 Force Change, −14 −30 −20 −1.4 −0.65 −22 −5.7 Humidity Aging: 14 Days @ 94° C. (200° F.) Max. Force, lbs. (avg.) Average 123.7 94.9 130.2 115.3 116.8 125.3 148.6 Coverage, % 88 75 93 90 90 90 95 Force Change, % −30 −39 −20 −29 −16 −25 −8.3 Humidity Aging: 21 Days @ 94° C. (200° F.) Max. Force, lbs.(avg.) Average 101.4 64.4 82.6 107.9 90.3 108.1 127.3 Coverage, % 87 75 70 77 83 83 93 Force Change, % −43 −59 −49 −34 −35 −35 −27

[0145] The original wire cord adhesion results show the standard formulation to have slightly higher adhesion than formulations containing resin/ester combinations. The formulations containing resin/ester combinations are all very similar except for the resin/ester combination of 8/4. At this time, the reason why this formulation has poorer original adhesion is not known.

[0146] The humidity aging results are interesting in that Examples 9, 11 and 12 have the highest force levels and lowest percent change from the original. Example 12 has a 50% increase in curing agent amount to offset the addition of ester to the compound. This formulation had the highest force recorded and the least change from the original adhesion. This suggests that an increase in the amount of curing agent can, along with the resin/ester combination, improve aged adhesion. All the resin/ester compounds except for Example 8 (resin 8/ester 8) exhibited lower changes in recorded force than the standard compound.

[0147] The formulation for Examples 6-12 are shown in Table III. TABLE III Example 6 Example 7 Example 8 Example 9 Example 10 Example 11 Example 12 SMR-L 100.00 ———————————————————————————

N326 60.00 ———————————————————————————

Kadox 930 10.00 ———————————————————————————

Cobalt Naphthenate 2.00 ———————————————————————————

Stearic Acid 1.20 ———————————————————————————

Santoflex 13 1.00 ———————————————————————————

PVI 0.20 ———————————————————————————

Pennacolite (3.85)/Resimene (4.23) 8.08 — — — — — — Cyrez ® CRA-148M — 8.08 8.00 8.00 8.00 8.00 8.00 SM RX-13804 — — 8.00 6.00 4.00 2.00 6.00 Subtotal 182.48 182.48 190.40 188.40 186.40 184.40 188.40 Mill Addition Sulfur 5.60 ———————————————————————

8.40 Vulkacit DZ 0.50 ———————————————————————

0.75 Total 188.58 188.58 196.50 194.50 192.50 190.50 197.55 Major Variable Cyrez ® CRA- Pennacolite 148M(8)/SM (3.85)/ Cyrez ® CRA- Cyrez ® CRA- Cyrez ® CRA Cyrez ® CRA- RX-13804(6)/ Resimene Cyrez ® CRA- 148M(8)/SM 148M(8)/SM 148M(8)/SM 148M(8)/SM Sulfur(8.4)/ (4.23) 148M RX-13804(8) RX-13804(6) RX-13804(4) RX-13804(2) Vulkacit (0.75) Example 6 Example 7 Example 8 Example 9 Example 10 Example 11 Example 12 Viscosity and Curing Properties Mooney Viscosity @ 168° C. (335° F.) Min. Viscosity 70.2 67.9 57.9 59.7 62.1 63.7 48.1 t5, minutes 1.4 1.8 1.9 1.8 2.2 2 1.7 t10, minutes 1.8 2 2.2 2.2 2.5 2.3 2 t35, minutes 2.9 2.6 2.8 2.8 3.3 2.9 2.6 Oscillating Disc Rheometer at 168° C. (335° F.) M_(L) 16.6 16.9 14.1 14.8 15.7 15.8 16 M_(H) 47.5 26.6 23.6 24.6 22.2 38.8 73.6 t_(s)2, minutes 1.4 1.8 1.8 1.8 1.8 1.8 1.6 tc(90), minutes 5.3 4.5 4.7 4.7 4.4 4.9 5.3 1.25*t′c(90), 6.7 5.6 5.8 5.8 5.5 6.2 6.7 minutes Cure Rate Index 25.6 36.4 35.2 35.2 37.5 31.6 26.7 Original Physical Properties Stress @ 100% 7.0 5.9 3.9 5.1 5.0 5.8 7.6 Elongation, MPa psi 1010 855 565 740 730 845 1105 Stress @ 200% 14.8 12.4 8.8 10.9 10.8 12.1 14.8 Elongation, MPa Stress @ 300% — 19.2 14.8 17.1 16.9 18.6 — Elongation, MPa Tensile Ultimate, 20.4 20.9 21.5 20.6 21.2 20.7 20.1 MPa psi 2960 3025 3116 2990 3080 3010 2915 Elongation @ 275 330 415 370 380 335 285 Break, % Hardness Duro 79 78 72 75 76 77 79 A, pts. Specific Gravity AVERAGE 1.204 AVERAGE AVERAGE AVERAGE — 1.203

[0148] The use of the resin/ester combination in a sulfur-cured natural rubber formulation can improve wire cord adhesion after heat aging and humidity aging as compared to a standard natural rubber formulation.

[0149] In order to verify that the increased cure system of Example 12 was not solely responsible for the increased adhesion performance of Example 12, an additional formulation, Example 13, was tested. The only difference between Examples 6 and 13 is that Example 13 has a 50% increase in the amount of cure system additives (Sulfur and Vulkacit). Table IV provides comparative data which demonstrates that increasing the cure system of the “control compound” (i.e., the prior art formulation of Example 6) by 50% does not lead to an increased adhesive effect. Accordingly, these data confirm that the increase in adhesion observed in Example 12 cannot solely be attributed to the increased amount of cure system additives, i.e., the increased adhesion is due to the adhesion promoter. TABLE IV Recipe Variable Pennacolite Cyrez ® Pennacolite(3.85)/ (3.85)/ CRA-148M(8)/ Resimene(4.23)/ Resimene SM RX-13804(6)/ Sulfur(8.4)/ (4.23) Sulfur(8.4)/ Vulkacit(0.75) “Control” Vulkacit(0.75) Example 13 Example 6 Example 12 SMR-L 100 ——————————

N 326 60 ——————————

Kadox 930 10 ——————————

Cobalt 2 ——————————

Napthenate Stearic Acid 1.20 ——————————

Santoflex 13 1.00 ——————————

PVI 0.20 ——————————

Pennacolite 8.08 8.08 — (3.85)/ Resimene(4.23) Cyrez ® CRA- — — 8.00 148M SM RX-13804 — — 6.00 Subtotal 182.48 182.48 188.40 Mill Addition Sulfur 8.40 5.60 8.40 Vulkacit 0.75 0.50 0.75 Total 191.63 188.58 197.55 Major Variable Cyrez ® Pennacolite(3.85)/ Pennacolite CRA-148M(8)/ Resimene(4.23)/ (3.85)/ SM RX-13804(6)/ Sulfur(8.4)/ Resimene(4.23) Sulfur(8.4)/ Processing Vulkacit(0.75) “Control” Vulkacit(0.75) Properties Example 13 Example 6 Example 12 Viscosity and Curing Properties Mooney Viscosity at 168° C. (335° F.) Minimum 69.3 77.2 66.4 Viscosity t5, minutes 1.3 1.2 1.3 t10, minutes 1.6 1.3 1.6 t35, minutes 2.3 1.9 2.2 Oscillating Disc Rheometer at 168° C. (335° F.) M_(L) 17 20 17.3 M_(H) 100.5 101.1 88.4 t_(s)2, minutes 1.4 1.5 1.7 t′c(90), minutes 6.7 9.6 5.9 1.25 * t′c(90), 8.3 12 7.4 mins. Cure Rate Index 19.1 12.4 23.5 Vulcanizate Properties Original Physical Properties Stress @ 100% 8.1 6.5 5.9 Elongation, MPa psi 1170 945 850 Stress @ 200% 15.7 13.7 11.5 Elongation, MPa Stress @ 300% — — 16.9 Elongation, MPa Tensile Ultimate, 18.4 20.1 18.7 MPa psi 2665 2920 2710 Elongation @ 240 300 330 Break, % Hardness Duro 82 80 80 A, pts. Specific Gravity 1.201 1.199 1.204 Adhesion to Steel Cord Original Properties: Maximum Force, lbs. (avg). Set 1 90.1 104.4 80.3 Set 2 78.4 99.3 80.6 Set 3 82.4 101.1 103.3 Average 83.6 101.6 88.1 Coverage, % 90 90 90

Adhesion Promoter Part III

[0150] Next, natural rubber-to-metal bonding was evaluated to determine the effect of added ester(s), as described herein. This presents a large potential for automotive parts, such as motor mounts, brakes, hoses, and the like.

[0151] The first study focused on long chain esters in natural rubber and their effect on adhesion to metal (see Table V—Examples 14-17). The data indicate that the adhesion promoters described herein improve adhesion to brass in a sulfur-cured rubber formulation. The use of the resin/ester combination did not improve adhesion versus compounds with ester only. TABLE V Example Example Example Example 14 15 16 17 SMR-L 100.00 ——————————

Kadox 930 5.00 ——————————

Stearic Acid 2.00 ——————————

N 330 35.00 ——————————

Cyrez ® CRA-148M 6.95 — 6.95 — RX-13804 6.95 5.00 6.95 — Subtotal 155.90 147.00 155.90 142.00 Mill Addition Sulfur 2.25 — — — Santocure TBSI 0.70 — — — DiCup 40KE — 5.00 ————————

Total 158.85 152.00 160.90 147.00 Major Variable RX-13804/ RX-13804/ Cyrez ® Cyrez ® Control CRA-148M RX-13804 CRA-148M Example Example 14 Example 15 Example 16 17 Viscosity and Curing Properties Mooney Viscosity at 335° F. (168° C.) Minimum 47.5 46.5 62 56 Viscosity t5, minutes 2 1.1 0.75 0.85 t10, minutes 2.3 1.3 0.85 1 t35, minutes 3 1.7 1.1 1.8 Oscillating Disc Rheometer at 335° F. (168° C.) M_(L) 13.4 12.4 11.4 13.1 M_(H) 41.9 67 74.2 74.6 t_(s)2, minutes 1.8 1.3 1.2 1.1 t′c(90), minutes 7.2 13.6 15.3 14.5 1.25 * t′c(90), 9 17 19.1 18.1 minutes Cure Rate Index 18.7 8.1 7.1 7.5 Original Physical Properties Stress @ 100% 2.0 4.0 5.5 5.1 Elongation, MPa psi 290 575 800 735 Stress @ 200% 5.6 14.7 — — Elongation, MPa Stress @ 300% 10.6 — — — Elongation, MPa Tensile 16.5 16.4 9.9 16.2 Ultimate, MPa psi 2390 2385 1440 2355 Elongation @ 440 215 140 190 Break, % Hardness Duro 52 57 62 61 A, pts. Specific Gravity 1.097 1.082 1.105 1.090 Metal Sulfur Peroxide Peroxide Peroxide Adhesion- ASTM D429 Brass Adhesion Force, 82.58 1.69 — — lbf/in width Failure Type R R R R % Failure 100 100 100 100 Aluminum Adhesion Force, — — — — lbf/in width Failure Type R R R R % Failure 100 100 100 100 Steel Adhesion Force, — — — — lbf/in width Failure Type R R R R % Failure 100 100 100 100

[0152] Table VI provides data wherein a sulfur cure system was used in formulations containing resin only (Example 18), a resin combined with a long chain ester of the disclosure (Example 20), and a control containing no resin and no ester (Example 19). From these data, it can be seen that the adhesion promoter system including a long chain ester and an adhesive resin performs best, and gives superior adhesive results when compared with the control formulation and the formulation containing the resin, but not including an ester of the disclosure. TABLE VI Recipe Variable Cyrez ® CRA Cyrez ® CRA Resin Resin 148M “Control” 148M/RX-13804 Example 18 Example 19 Example 20 SMR-L 100 —————————————

Kadox 930 5.00 —————————————

Stearic Acid 2.00 —————————————

N 330 35.00 —————————————

Cyrez ® Resin 7.00 — 7.00 148-M RX-13804 — — 7.00 Subtotal 149.00 142.00 156.00 Mill Addition Sulfur 2.25 2.25 2.25 Santocure TBSI 0.70 0.70 0.70 Total 151.95 144.95 158.95 Viscosity and Curing Properties Mooney Viscosity at 168° C. (335° F.) Minimum 48.1 53.2 48.2 Viscosity t5, minutes 2.1 1.5 2 t10, minutes 2.4 1.8 2.3 t35, minutes 3.2 2.6 2.9 Oscillating Disc Rheometer at 168° C. (335° F.) M_(L) 13.7 14.6 13.5 M_(H) 31.2 36 40.9 t_(s)2, minutes 1.8 1.7 1.8 t′c(90), minutes 5.3 5.3 7.1 1.25 * t′c(90), 6.7 6.7 9 mins. 28.6 27.3 19 Cure Rate Index Vulcanizate Properties Original Physical Properties Stress @ 100% 1.9 1.8 2.0 Elongation, MPa psi 280 255 300 Stress @ 200% 4.7 4.5 5.6 Elongation, MPa Stress @ 300% 8.6 8.8 10.6 Elongation, MPa Tensile Ultimate, 22.1 24.5 16.5 MPa psi 3205 3560 2380 Elongation @ 555 565 440 Break, % Hardness Duro 57 55 52 A, pts. Specific Gravity — — 1.097 Metal Adhesion - ASTM D249 Brass Adhesion Force, 118.2 46.3 138.9 lbf/in width Failure Type R, RM R R, RM % Failure Type 95, 5 100 95, 5 Aluminum Adhesion Force, Fail Fail Fail lbf/in width Failure Type RM RM RM % Failure 100 100 100 Steel Adhesion Force, Fail Fail Fail lbf/in width Failure Type RM RM RM % Failure 100 100 100

[0153] Next, the effect of the long chain esters described herein was evaluated in an EPDM rubber formulation for rubber to metal bonding. The cure system was also evaluated to determine the effect of peroxide versus a sulfur system. The sulfur formulations did not work, thus these formulations were discarded. The peroxide cured formulations were varied by using the ester alone and the resin/ester combination. The data below in Table VII (Examples 21-23), lists adhesion results for brass, aluminum and steel cord in EPDM. TABLE VII Major Variable RX-13804/ Cyrez ® RX-13804 CRA-148M Control Example 21 Example 22 Example 23 Brass Adhesion Force, 1.26 52.43 — lbf/in. width Failure Type R R R % Failure 100 100 100 Aluminum Adhesion Force, — — — lbf/in. width Failure Type R R R % Failure 100 100 100 Steel Adhesion Force, 16.82 19.97 — lbf/in. width Failure Type R R R % Failure 100 100 100

[0154] The formulation containing the resin/ester has significantly greater adhesion to brass than the formulation with just ester, and the control. The steel adhesion results show that the formulation with ester does provide some adhesion, but the resin/ester combination is unexpectedly better. The control formulation has no adhesion to steel. None of the formulations has adhesion to aluminum.

[0155] The recipe/formulation data for Examples 21-23 is shown in Table VIII: TABLE VIII Example 21 Example 22 Example 23 Nordel IP 3720 100 ————————

N 762 56 ————————

Kadox 930 5.00 ————————

Ricon 150 5.00 ————————

SR 350 4.00 ————————

RX-13804 10.00 7.00 — Cyrez ® Resin — 10.00 — 148M Subtotal 180.00 187.00 170.00 Mill Addition VulCup 40KE 7.00 ————————

Total 187.00 194.00 177.00 Major Variable RX-13804/ Cyrez ® RX-13804 CRA-148M Control Example 21 Example 22 Example 23 Peroxide Cure Viscosity and Curing Properties Mooney Viscosity at 168° C. (335° F.) Minimum 23.9 29.6 33.6 Viscosity t5, minutes 9.5 11.2 7.5 t10, minutes 10.7 11.9 7.9 t35, minutes — 15.8 8.8 Oscillating Disc Rheometer at 168° C. (335° F.) M_(L) 6.6 12.2 9.2 M_(H) 87.1 92.4 177 t_(s)2, minutes 0.92 0.92 0.83 t′c(90), minutes 6.5 8.4 8.5 1.25 * t′c(90), 8.1 10.5 10.6 minutes Cure Rate Index 17.9 13.3 13 Original Physical Properties Stress @ 100% 1.4 6.5 13.7 Elongation, MPa psi 198 940 1990 Stress @ 200% 11.2 12 — Elongation, MPa Stress @ 300% — — — Elongation, MPa Tensile Ultimate, 12.2 13.0 19.7 MPa psi 1770 1890 2860 Elongation @ 200 210 135 Break, % Hardness Duro A, 80 83 86 pts. Specific Gravity 1.099887 1.122098 1.114178

[0156] Table IX provides comparative data that supplements the data presented in Table VIII. Example 24, contains resin, but does not contain any of the long chain esters disclosed herein. As can be seen from the data of Table IX, Example 24 did not promote adhesion between EPDM and metal substrates.

[0157] Table IX also contains formulations wherein the ester was varied. A saturated ester, UBS 020602, in accordance with the disclosure, was used to formulate Examples 25 and 26. In Example 25, the saturated ester additive was not combined with an adhesive resin as described herein, and failed to promote adhesion between EPDM and the metal substrates. However, in Example 26, the saturated ester was combined with an adhesive resin, and excellent adhesion between metal substrates and EPDM, more particularly between steel and EPDM, was obtained. TABLE IX Recipe Variable RX-13804/ UBS 020602/ Cyrez ® Cyrez ® Cyrez ® CRA-148M CRA-148M UBS 020602 CRA-148M Control Example 22 Example 24 Example 25 Example 26 Example 23 Nordel IP 3720 100.00 ————————————————————

N 762 56.00 ————————————————————

Kadox 930 5.00 ————————————————————

Ricon 150 5.00 ————————————————————

SR 350 4.00 ————————————————————

RX 13804 7.00 — — — — Cyrez ® 10.00 10.00 — 10.00 — Resin 148M UBS 020602 — — 7.00 7.00 — Subtotal 187.00 180.00 177.00 187.00 170.00 Mill Addition Vulcup 40 KE 7.00 ————————————————————

Total 194.00 187.00 184.00 194.00 177.00 Recipe Variable UBS 020602 Cyrez ® Cyrez ® Processing RX-13804/148M CRA-148M UBS 020602 CRA-148M Control Properties Example 22 Example 24 Example 25 Example 26 Example 23 Viscosity and Curing Properties Mooney Viscosity at 121° C.(250° F.) Minimum Viscosity 26.3 32.6 23.4 26.6 28.7 t5, minutes 12.8 9.8 11.4 11.1 9.7 t10, minutes 14.2 10.4 12.3 11.8 10.2 t35, minutes FAIL 12.7 17.8 14.8 11.4 Oscillating Disc Rheometer at 177° C.(350° F.) M_(L) 6.7 10.8 6.7 8 8.8 M_(H) 74.1 115.9 129 87.4 171.6 t₅2, minutes 0.92 0.92 1.1 1 1 t′c(90), minutes 7.4 10.1 9.1 9.3 10.3 1.25 * c(90), 9.3 12.6 11.4 11.6 12.9 minutes Cure Rate index 15.4 10.9 12.5 12.1 10.7 Vulcanizate Properties Original Physical Properties Stress @ 100% 6.1 9.3 8.4 6.3 13.4 Elongation, MPa psi 890 1350 1220 920 1945 Stress @ 200% 11.7 — — — — Elongation, MPa Stress @ 300% — — — — — Elongation, MPa Tensile Ultimate, 12.3 15.2 14.1 12.0 18.2 MPa psi 1785 2200 2045 1735 2635 Elongation @ 205 160 145 180 125 Break, % Hardness Duro 85 87 85 83 87 A, pts. Specific Gravity 1.119 1.128 1.102 1.120 1.110 Metal Adhesion - ASTM D429 Brass Adhesion Force, 91 61.5 FAIL 77.6 FAIL lbf/in width Failure Type R R RM R RM % Failure 100 100 100 100 100 Aluminum Adhesion Force, FAIL FAIL FAIL FAIL FAIL lbf/in width Failure Type RM RM RM RM RM % Failure 100 100 100 100 100 Steel Adhesion Force, FAIL 35.3 FAIL 77 FAIL lbf/in width Failure Type R RM RM RM-R RM % Failure 100 100 100 67%, 33% 100

EPDM Rubber to Metal Bonding

[0158] Additional esters were evaluated to determine their effect on adhesion when combined with an adhesive resin. The esters evaluated were as follows: Plasthall DOS A saturated diester based on 2-ethylhexyl alcohol and sebacic acid. RX-13577 An unsaturated monoester based on tridecyl alcohol and tall oil fatty acid. RX-13824 An unsaturated dimerate ester based on tridecyl alcohol and a C-36 dimer acid. This ester is similar to RX-13804, which uses the same dimer acid, but RX-13804 is reacted with 2-ethylhexyl alcohol (di-2-ethylhexyl dimerate).

[0159] The results indicate that the compound with DOS/resin provides good adhesion to brass and steel. The RX-13577/resin compound has excellent adhesion to brass and steel, and the force values for steel are greater than any of the other ester/resin combinations. The data suggests that a greater degree of ester unsaturation levels provides greater adhesion because RX-13577 does have more unsaturated sites by weight than RX-13804 or RX-13824. Another piece of data that helps support the above statement is the steel adhesion data for the ester only compounds. The RX-13577 compound had the only measurable adhesion while DOS and RX-13824 had no adhesion values.

[0160] The data is set forth in Table X, Examples 27-34: TABLE X Example 27 Example 28 Example 29 Example 30 Example 31 Example 32 Example 33 Example 34 Nordel IP 3720 100.00 —————————————————————————

N 762 56.00 —————————————————————————

Kadox 930 5.00 —————————————————————————

Ricon 150 5.00 —————————————————————————

SR 350 4.00 —————————————————————————

Plasthall DOS 10.00 7.0 — — — — — — Cyrez ® CRA-148M — 10.00 7.00 — 10.00 — 10.00 — RX-13577 — — — 10.00 7.00 — — — RX-13824 — — — — — 10.00 7.00 — Control — — — — — — — — Subtotal 180.00 187.00 177.00 180.00 187.00 180.00 187.00 170.00 Mill Addition Vulcup 40KE 7.00 —————————————————————————

TOTAL 187.00 194.00 184.00 187.00 194.00 187.00 194.00 177.00 Major Variable Plasthall Plasthall DOS/Cyrez ® RX-13577/ RX-13824/ DOS CRA- Cyrez ® CRA- Cyrez ® CRA- Cyrez ® (dioctylsebacate) 148M 148M RX-13577 148M RX-13824 CRA-148M Control Example 27 Example 28 Example 29 Example 30 Example 31 Example 32 Example 33 Example 34 Plasticizer Processing Properties Viscosity and Curing Properties Mooney Viscosity at 250° F. (121° C.) Min. 19.9 26.1 32.2 21.1 26.1 21.3 26.8 30.9 Viscosity t5, minutes 8.6 9.6 8.4 7.6 7.3 8.9 7.8 6.6 t10, minutes 9.3 11.8 8.9 8.6 7.9 9.8 8.3 6.9 t35, minutes FAIL FAIL 17.6 FAIL FAIL FAIL 10.2 8.3 Oscillating Disc Rheometer at 350° F. (177° C.) M_(L) 5.5 6.6 10 6.6 7.2 6.4 8.6 9.7 M_(H) 88.6 63.1 84.9 58.8 52.8 75.3 58.5 125.8 t_(s)2, minutes 0.92 0.92 0.92 1.3 0.92 1 0.92 0.83 t′c(90), mins. 6.3 6 6.1 6.9 6 6.1 5.9 6.3 1.25 * t′c(90), 7.8 7.5 7.6 8.7 7.5 7.6 7.4 7.8 minutes Cure Rate 18.8 19.7 19.4 17.6 19.7 19.7 20 18.5 Index Original Physical Properties Stress @ 100% 4.8 5.0 6.4 3.8 4.5 4.2 4.7 8.2 Elongation, MPa psi 700 725 925 545 655 615 680 1195 Stress @ 200% 11.4 9.4 12.3 7.5 7.8 9.7 8.2 — Elongation; MPa Stress @ 300% — — — 11.1 10.4 — — — Elongation; MPa Tensile 13.5 11.1 13.9 12.7 10.4 11.7 10.4 18.1 Ultimate, MPa psi 1960 1650 2010 1835 1515 1690 1515 2620 Elongation @ 220 250 225 320 300 235 275 175 Break, % Hardnes Dura 81 84 86 79 82 80 82 85 A, pts. Specific 1.102 1.123 1.125 1.098 1.118 1.098 1.121 1.113 Gravity Example 27 Example 28 Example 29 Example 30 Example 31 Example 32 Example 33 Example 34 Metal Adhesion - ASTM D429 Brass Adhesion — 128.1 51.1 — 139.4 — 133.5 — Force, lbf/in width Failure Type RM RM R RM R RM R RM % Failure 100 100 100 100 100 100 100 100 Aluminum Adhesion — — — — — — — — Force, lbf/in width Failure Type RM RM RM RM RM RM RM RM % Failure 100 100 100 100 100 100 100 100 Steel Adhesion — 37.3 — 14.2 96.7 — 42.3 — Force, lbf/in width Failure Type RM RM RM RM RM RM RM RM % Failure 100 100 100 100 50 100 100 100

Chlorinated Polyethylene Rubber to Polyester Cord

[0161] More specifically, RX-13845 was evaluated for cord or fabric to rubber adhesion. RX-13845 is an adhesion promoter system consisting of 36 wt. % RX-13804, 36 wt. % Cyrez CRA-138 Resin (a liquid at room temperature), and 28% substrate (synthetic calcium silicate). RX-13845 was prepared by adding preheated Cyrez CRA 138 resin liquid to a dry carrier (substrate) contained in a mixing bowl, followed by addition of preheated RX-13804. The materials were mixed at low speed for 3 minutes. The materials were blended for an additional 3 minutes. RX-13845 permits liquids to be handled as powders. Because the active adhesion promoter is released, the active ingredient is released from the carrier, incorporation of RX-13845 into a rubber compound allows the adhesion promoter to function in the same manner as if it had been incorporated into rubber as a neat material.

[0162] The results demonstrate a significant improvement in adhesion of untreated nylon fibers, isocyanate treated nylons, isocyanate treated aramid fibers, and untreated polyester fibers to chlorinated polyethylene polymer. The data is set forth in Table XI, Examples 34-38. TABLE XI Example Example Example Example 35 36 37 38 Tyrin CPE CM 0730 100.00 —————————————

N 774 Carbon Black 55.00 —————————————

N 650 Carbon Black 30.00 —————————————

Albacar 5970(CaCO₃) 10.00 —————————————

PARAPLEX ® G-62 15.00 —————————————

PLASTHALL ® TOTM 30.00 —————————————

Calcium Oxide 4.40 —————————————

Flectol TMQ 0.20 —————————————

RX-13845 — 3.00 6.00 10.00 Subtotal 244.60 247.60 250.60 254.60 Mill Addition Vulcup 40KE 9.50 —————————————

Triganox 17/40 3.50 —————————————

PLB 5405(75%) 6.70 —————————————

Total 264.30 267.30 270.30 274.30 Major Variable RX-13845 RX-13845 RX-13845 Control (3) (6) (10) Viscosity and Curing Properties Mooney Viscosity at 132° C. (270° F.) Minimum Viscosity 40.7 40.4 38.2 37.0 t5, minutes 2.2 2.2 2.3 2.3 t10, minutes 2.5 2.5 2.5 2.5 t35, minutes 3.0 3.0 3.2 3.0 Oscillating Disc Rheometer at 160° C. (320° F.) M_(L) 9.4 11.9 10 9.4 M_(H) 48.7 42.2 38.4 37 t_(s)2, minutes 1.3 1.2 1.7 1.5 t′c(90), minutes 25.8 28.3 29.7 21.8 1.25 * t′c(90), minutes 32.3 35.4 37.1 27.3 Cure Rate Index 4.1 3.7 3.6 4.9 Original Physical Properties Stress @ 100% 6.4 6.2 6.3 5.4 Elongation, MPa psi 930 905 920 790 Stress @ 200% 11.7 10.9 11.1 9.2 Elongation, MPa Stress @ 300% — — — — Elongation, MPa Tensile Ultimate, MPa 13.5 12.5 12.8 10.5 psi 1965 1820 1850 1530 Elongation @ Break, % 250 255 250 275 Hardness Duro A, pts. 80 80 80 78 Specific Gravity 1.323 1.326 1.324 1.324 UNTREATED NYLON Average Adhesion Force, 8.43 7.97 9.63 10.13 lbf/in width std.dev 1.31 1.60 1.23 1.19 ISOCYANATE TREATED NYLON Average Adhesion Force, 24.84 27.90 30.24 34.93 lbf/in width std.dev 1.51 4.56 4.54 3.95 Rubber Failure ———————————

UNTREATED ARAMID Average Adhesion Force, 5.54 4.09 6.44 4.80 lbf/in width std.dev 0.57 1.12 0.76 0.46 ISOCYANATE TREATED ARAMID Average Adhesion Force, 5.50 8.20 9.78 9.32 lbf/in width std.dev 0.31 1.03 2.27 0.88 UNTREATED POLYESTER Average Adhesion Force, 8.90 9.72 17.77 17.39 lbf/in width std.dev 1.33 0.33 4.59 6.49

Method of Measuring Cord Adhesion

[0163] Esters were evaluated to determine their effect on adhesion of cords to rubbers when combined with an adhesive resin. The following method is for determining the relative strip-peel adhesion of reinforcing fibers, including natural and manmade filaments and spun yams, to various rubber compounds and elastomers. This method is conventionally used with industrial weight fibers of 500 denier or greater. Typically, the most common elastomers and compounds employed are natural rubber, styrene butadiene rubber, copolymers of olefins with non-conjugated dienes (EPDM), polychloroprene rubber (CR), acrylonitrile butadiene elastomer (NBR), chlorosulphonated polyethylene elastomer (CSM), polyisoprene rubber, isobutylene-isoprene copolymeric rubber, chlorinated isobutylene-isoprene copolymeric rubber, brominated isobutylene-isoprene copolymeric rubber, polyvinylchloride, urethane, and blends thereof, but this technique can be modified to determine fiber adhesion to a wide variety of materials.

[0164] The adhesion testing described herein was performed in accordance with ASTM D 4393-85 “Strap Peel Adhesion of Reinforcing Cords or Fabrics to Rubber Compounds.”

[0165] Typically, 1″×5″ strips of fiber/rubber composite materials were prepared for testing. Fibers were positioned onto a tape backing using a rotatable cylinder. The tape backing was applied to a milled elastomer or rubber compound under high temperature and pressure in a hydraulic press (i.e., at curing, extruding, or other conditions) to form a cord- or fabric-reinforced composite material. The composite was then cut into strips for adhesion measurements (e.g., through separation load values, appearance, etc.).

[0166] Procedure

[0167] An ASTM 429 mold was placed in a compression press (capable of achieving temperatures between 250° F. and about 400° F., and a pressure of about 125 tons) and the temperature was set within ±2° F. of the vulcanization temperature (cure temperature) for the specific rubber compound used. The press was maintained within the specified temperature range for about 30 minutes.

[0168] Three strips of 3″ wide masking tape (a suitable masking tape is #515 Masking Tape, Anchor Continental, Inc. Columbia, S.C.), with adhesive side out, were wrapped around the rotatable cylinder. The three strips were overlapped to achieve a tape backing having a total width of about 7″. Six 1″ wide fiber samples were wrapped onto the tape backing. The same or different yarn samples can be wound onto each tape backing. Each fiber or cord sample should be wound, however, such that there is no overlapping of fibers and no space between adjacent fibers. Typically, three strips of each fiber sample were prepared and tested.

[0169] The fibers were secured with 1″ wide masking tape, and the strips were marked A, B, C, D, E, and F. The six wound samples were removed from the cylinder by cutting across the cylinder.

[0170] A 5″×7″ piece of unvulcanized compounded rubber to be tested, which has been milled to a specified thickness (0.250±0.20 inches), was cut. The mold surface which will be in contact with the fiber assembly was cleaned with n-heptane.

[0171] The preheated mold was removed from the press. The fiber samples were placed at the bottom mold plate with the masking tape backing face down, and the fibers facing up. A 1″×7″ strip of aluminum foil was placed on the back edge of the fiber samples so that the fibers are perpendicular to the aluminum foil and about one inch of their length covers the aluminum foil strip. Each strip has a specified position in the press. The cleaned 5″×7″ unvulcanized rubber slab was then on top on the fiber assembly. The preheated top mold plate was placed on top of the samples to form a sandwich of mold top plate, rubber compound, aluminum foil, yarn samples, tape and bottom plate. This sandwich is then placed in the preheated compression press and a pressure of about 125 tons is applied. The pressure and temperature are maintained for the specified time (cure time).

[0172] The mold assembly was removed from the press at the end of the cure time. It is important not to disturb the fiber composite while separating the pad from the mold plates. Typically, the pad was placed in cold water to expedite the cooling process. The pad was cooled to ambient temperature prior to marking the pad for identification.

[0173] The adhesion pad should sit for an extended period (“conditioning period”), e.g., overnight, prior to cutting into the 1″×5″ strips for adhesion testing. As much of the aluminum foil strip as possible was removed to give a starting separation between the fiber sample and the rubber compound. The foil can be left in place if too difficult to remove. After conditioning, each 5″×7″ rubber section was cut into six 1″×5″ strips such that only one fiber to be tested is contained in each strip.

[0174] Each 1″×5″ adhesion composite strip was tested on the Instron 4201 tensile/compression machine (Instron Corporation, Canton, Mass.) according to method 08 of the Instron Series IX Materials Testing™ Software. TABLE XII Material Chemical Description Supplier SMR-L Natural rubber Alcan Kadox 930 Zinc Oxide The C. P. Hall Company Stearic Acid R. G. Stearic Acid, rubber grade The C. P. Hall Company N-330 Carbon Black JM Huber or Degussa Spider Sulfur Elemental Sulfur The C. P. Hall Company Santocure TBSI N-tert-butyl-di(2- Harwick Standard benzothiazolesulfen)imide RX-13577 Tridecyl tallate The C. P. Hall Company RX-13804 Di(2-ethylhexyl)dimerate The C. P. Hall Company RX-13824 Ditridecyl Dimerate The C. P. Hall Company Plasthall DOS Dioctyl sebacate The C. P. Hall Company Paraplex A-8000 Polyester Adipate The C. P. Hall Company Staflex DBM Dibutyl maleate The C. P. Hall Company DiCup 40 KE Dicumyl Peroxide on Burgess Clay Hercules RX-13845 36% RX-13804, 36% Cyrez ® D- The C. P. Hall Company 148M, 28% Hydrated Amorphous Silica Cyrez ® Resin D-148M Melamine Resin Powder Cytec Concentrate N-326 Carbon Black JM Huber Cobalt Naphthenate Metal Carboxylate adhesion Sheperd promoter Santoflex 13 N-Isopropyl-N′-phenyl-p- Harwick phenylenediamine PVI N-(cyclohexylthio) phthalimide Flexsys Pennacolite Resin Formaldehyde Resin Indspec Vulkacit DZ Benzothiazl-2-dicyclohexyl- Bayer sulfenamide Resimene Hexamethoxymelamine Solutia Nordel IP3720 Hydrocarbon Rubber DuPont N762 Carbon Black JM Huber Ricon 150 Liquid Polybutadiene Ricon TMTD Tetramethyl thiuram disulfide R. T. Vanderbilt Rotax 2-mercaptobenzothiazole R. T. Vanderbilt SR 350 Acrylic Ester Sartomer UBS020602 Di(2-ethylhexyl) dimerate, The C. P. Hall Company hydrogenated Cyrez ® Resin CRA- Melamine Resin Powder Cytec 133M concentrate Cyrez ® Resin CRA- Melamine Resin Powder Cytec 148M concentrate Royalene 501 Ethylene-propylene ethylidene Uniroyal norbornene rubber 57/43 EP Ratio Royalene 502 ENB third monomer 62/38 EP ratio Uniroyal N-550 Carbon Black Engineering Carbon RX-13782 Capric Tallate The C. P. Hall Company RX-13805 Di(2-ethylhexyl) dimerate The C. P. Hall Company RX-13806 Didecyl dimerate The C. P. Hall Company RX-13853 Di-hexyldecyl tallate The C. P. Hall Company UBS 020602 Di (2-ethylhexyl) dimerate (Pripol The C. P. Hall Company 1006) UBS 120601 polyester dimerate The C. P. Hall Company UBS 121201 polyester dimerate The C. P. Hall Company Sunpar 2280 Paraffinic Oil Sun Oil Premix MBT 2-mercaptobenzothiazole The C. P. Hall Company Premix TMTD Tetramethyl thiuram disulfide The C. P. Hall Company Premix DPTT Dipentamethylene thiurum The C. P. Hall Company (tetra)sulfide Premix TDEC Tellurium diethyldithiocarbamate The C. P. Hall Company UBS051602 Dioleyl dimerate The C. P. Hall Company UBS060302 Ditridecyl dimerate The C. P. Hall Company BM050702 Pentaerythritol tetratallate The C. P. Hall Company Royalene IM7200 blend of ethylene-propylene- Uniroyal ethylidene norbornene rubber with polyethylene dust 76/24 EP Ratio RX-13822 Tridecyl dimerate The C. P. Hall Company RX-13823 Polyester dimerate The C. P. Hall Company Trigonox 145-45B-pd 2,5-dimethyl-2,5-di-(tert- Akzo Nobel butylperoxy)hexyne-3, 45% supported on calcium carbonate Tyrin CPE CM 0730 chlorinated polyethylene 30% Dupont Dow chlorine N-774 carbon black Degussa Engineered Carbons N-650 carbon black Degussa Engineered Carbons Albacar 5970 calcium carbonate The C. P. Hall Company Paraplex G-62 epoxidized soybean oil The C. P. Hall Company RX-13845 Micro Cel E 28 wt. %, RX-13804 36 The C. P. Hall Company wt. %, Cyrez ® CRA-138M 36 wt. % Micro Cel E Calcium Silicate The C. P. Hall Company Cyrez ® CRA-138M Melamine Formaldehyde resin Cytec Cyrez ® CRA-148M Melamine Formaldehyde resin Cytec VulCup 40KE 2,2′-bis(tert-butylperoxy Harwick Standard diisopropylbenzene Triganox 17/40 4,4-bis(tert-butyl peroxy)-3,3,5- Akzo Nobel trimethylcyclohexane PLB 5405 (75%) Trimethylolpropane trimethyl Flow Polymer Incorporated acrylate SMR CV 60 Natural Rubber Process Oil C-255E Parraffinic Oil The C. P. Hall Company RX-13896 Di(2-ethylhexyl) dimerate The C. P. Hall Company (Unidyme 22) Sulfur Sulfur The C. P. Hall Company Santocure TBBS N-t-butyl-2- Harwick Standard benzothiazolesulfenamide Hallco TE-577 Tridecyl Tallate The C. P. Hall Company RX-13653 pentaerythritol tetratallate The C. P. Hall Company RX-13892 Diolelyl dimerate The C. P. Hall Company Calcium Oxide Calcium Oxide The C. P. Hall Company Plasthall TOTM 72 wt. % Trioctyl Trimellitate, 28 The C. P. Hall Company wt. % Hydrated Amorphous Silica Flectol TMQ 2,2,4-Trimethyl-1,2- Flexsys dihydroquinoline, polymerized Untreated nylon fiber Beaver Manufacturing Co. Powerloc Isocyanate treated nylon fiber Beaver Manufacturing Co. Untreated aramid fiber Beaver Manufacturing Co. Beaverloc Isocyanate treated aramid fiber Beaver Manufacturing Co. Untreated polyester fiber Beaver Manufacturing Co.

[0175] In accordance with an important feature of the compositions, methods and articles described herein, the combination of one or more of the long chain esters described herein and combined with the melamine- or phenol-containing adhesive resin (the combination being referred to herein as the “adhesion promoter” or “adhesion promoter system”) can be used in liquid form by providing the ester/resin adhesion promoter in solution (1) by solubilizing both components with one or more suitable organic solvents or (2) by emulsifying the ester and resin components in water with one or more suitable emulsifying agents. The water-based emulsion should have an HLB value of about 4 to about 5 for best ester dispersion in the emulsion. In liquid form, the adhesion promoter has a number of advantages, particularly the ability to coat a substrate, such as a metal or polymeric substrate, with the liquid ester/resin adhesion promoter for adherence of an elastomer to the substrate, without changing the composition of the elastomer. Other advantages include (1) the ability to prepare a concentrated, master batch of the adhesion promoter having a relatively high concentration, e.g., 50-90% by weight of the adhesion promoter that can be diluted upon addition to an elastomeric composition or upon substrate coating; (2) the ability to include excess alcohol, e.g., 2-ethylhexanol, during the synthesis of the long chain ester portion of the liquid adhesion promoter, for use as a solvent for solubilizing the resin portion of the liquid adhesion promoter. The use of excess alcohol during the synthesis of the esters is particularly advantageous for ester synthesis since the esterification reaction proceeds faster with excess alcohol. Since the excess alcohol is useful in solubilizing the resin, the excess alcohol can remain with the synthesized ester without removing much, or any, of the excess alcohol in an ester concentration or purification step.

[0176] The liquid adhesion promoter, whether solubilized in an organic liquid or emulsified in a water-based emulsion, can be added to the elastomeric composition for adhesion to a substrate, e.g., a metal, polymeric layer, film, or fibrous, e.g., fabric, substrate, or can be used to pre-treat, e.g., coat, the substrate, e.g., a metal or a polymeric layer, film, fibrous or fabric substrate for adhesion of the elastomer thereto. In another embodiment, the substrate, for example, polymeric sheets, films, fibers, yarns and/or fabrics, e.g., nylon, glass, ARAMID, or polyester, can be pretreated with the resin component of the adhesion promoter system (known in the art as an “isocyanate pretreatment”) for adhesion of the substrate to an elastomer. The resin-treated substrate then can be treated with the ester component of the adhesion promoter system for improved adherence of the elastomer to the substrate. The resin-treated substrate can be ester treated in any manner, preferably by dipping or coating the resin-treated substrate with an organic solution of the ester or a water-based emulsion containing the ester. Alternatively, the ester can be added to the elastomer for contact with and adherence to the resin-treated substrate, or the ester and resin combination (adhesion promoter system) can be applied to the substrate as a coating, which preferably is dried prior to contact with the elastomer. As previously disclosed, the adhesion promoter system can be added directly to the elastomer composition.

[0177] The organic solution (RX-13928, hereinafter “Solution”) and water-based emulsion (RX-13937 hereinafter “Emulsion”) versions of the liquid adhesion promoters described herein; were tested for adherence to various elastomers. The organic solution version of the adhesion promoter was tested (1) by adding the organic solution directly to the elastomer compositions, and (2) by pre-treating the substrate with the combined ester/resin adhesion promoter composition. The water-based emulsion was tested only by pre-treating the substrate prior to elastomer adherence. The data are shown in the following Tables XIII to XV. In the following Tables XIII to XV, substrates pre-treated with the liquid adhesion promoter compositions (whether organic solution or water-based emulsion) were oven dried for 30 hours at 65° C. prior to applying the elastomer. TABLE XIII Solvent Based Liquid Adhesion Promoter For Brass Recipe Control Solution Solution RX-13804 RX-13892 1 2 3 4 5 Elastomer Composition (Parts by wt.) Nordel IP 100.00 3720 (EPDM) N 762 56.00 Kadox 930 5.00 Ricon 150 5.00 SR 350 4.00 Solution — 8.00 10.00 — RX-13804 — — — 4.00 — RX-13892 — — — — 4.00 Subtotal 170.00 178.00 180.00 174.00 174.00 Mill Addition (Parts by wt.) VULCUP 7.00 40KE Total 177.00 185.00 187.00 181.00 181.00 Major Variable Control Solution Solution RX-13804 RX-13892 Processing Properties Mooney Viscosity at 120° C. (250° F.) Minimum 28.4 22.8 21.1 25.0 24.6 Viscosity t5, minutes 8.9 8.9 9.3 9.4 9.9 t10, minutes 9.4 9.5 10.0 10.0 10.6 t35, minutes 11.0 >60 >60 12.3 >60 Oscillating Disc Rheometer at 177° C. (350° F.) M_(L) 8.0 6.4 6.5 7.8 7.9 M_(H) 110.5 86.0 82.1 99.9 105.4 t_(s)2, minutes 0.9 1.0 1.0 1.0 1.0 t'c(90), 6.4 6.8 7.2 7.3 8.4 minutes 1.25 * 8.0 8.5 9.0 9.2 10.5 t'c(90), minutes Cure Rate 18.2 17.2 16.2 15.8 13.5 Index Recipe JEKS1-170 Major Variable Control Solution Solution RX-13804 RX-13892 Original Physical Properties Stress @ 11.2 6.2 5.8 8.0 8.3 100% Elongation, MPa psi 1625 905 840 1155 1205 Tensile 16.7 14.2 12.2 15.7 15.2 Ultimate, MPa psi 2415 2060 1770 2280 2205 Elongation 135 195 195 170 165 @ Break, % Hardness 85 82 82 83 84 Duro A, pts. Specific 1.1058 1.104 1.103 1.104 1.101 Gravity Metal Adhesion- ASTM D429 Solution Treated Brass (painted brass - like primer) Adhesion 60.03 74.12 16.23 77.4 71.43 Force, lbf/ in. width Failure Type R R RM R R % Failure 100 55 100 100 100 Emulsion Treated Brass Adhesion Fail Fail 20.64 39.02 54.94 Force, lbf/ in. width Failure Type RM RM RM RM R % Failure 100 100 100 100 100

[0178] TABLE XIV Water-Based Emulsion Liquid Adhesion Promoter For Brass Recipe JEKS1-150 Control 1 Emulsion 2 Emulsion 3 Nordel IP 3720 100.00 100.00 100.00 N 762 56.00 56.00 56.00 Kadox 930 5.00 5.00 5.00 Ricon 150 5.00 5.00 5.00 SR 350 4.00 4.00 4.00 Emulsion 8.00 10.00 Subtotal 170.00 178.00 180.00 Mill Addition VULCUP 40KE 7.00 7.00 7.00 TOTAL 177.00 185.00 187.00 Emulsion Emulsion Major Variable Control 8.00 10.00 Viscosity and Curing Properties Mooney Viscosity at 121° C. (250° F.) Minimum Viscosity 28.00 26.4 26.4 t5, minutes 10.5 13.4 9.8 t10, minutes 11.0 14.5 10.3 t35, minutes 12.7 18.9 >60.0 Oscillating Disc Rheometer at 177° C. (350° F.) M_(L) 12.3 11.5 11.6 M_(H) 120.5 86.3 73.7 t_(s)2, minutes 0.9 0.9 1.0 t′c(90), minutes 7.0 8.5 7.5 1.25 * t′c(90), minutes 8.8 10.6 9.4 Cure Rate Index 16.5 13.2 15.4 Original Physical Properties Stress @ 100% Elongation, MPa 10.9 6.5 5.6 psi 1575 945 810 Stress @ 200% Elongation, MPa — 13.3 10.4 Stress @ 300% Elongation, MPa — — — Tensile Ultimate, MPa 16.8 13.3 10.9 psi 2440 1935 1585 Elongation @ Break, % 135 200 210 Hardness Duro A, pts. 84 84 84 Specific Gravity 1.113 1.110 1.111 Metal Adhesion - ASTM D429 Adhesion Force, lbf/in. width Fail 22.8 23.3 Failure Type RM RM RM % Failure 100 100 100

[0179] TABLE XV Liquid Adhesion Promoter System For ARAMID Fiber Recipe JEKS1-100 1 Elastomer Composition (chlorinated polyethylene) Tyrin CP 0730 100.00 N 774 Carbon Black 55.00 N 650 Carbon Black 30.00 Albacar 5970(CaCO₃) 10.00 PARAPLEX G-62 15.00 PLASTHALL TOTM 30.00 Calcium Oxide 4.40 Flectol TMQ 0.20 Subtotal 244.60 Mill addition Vulcup 40KE 9.50 Triganox 17/40 3.50 PLB 5405(75%) 6.70 TOTAL 264.30 Major Variable Control Viscosity and Curing Properties Mooney Viscosity at 132° C. (270° F.) Minimum Viscosity 40.2 t5, minutes 2.5 t10, minutes 3.0 t35, minutes 4.8 Oscillating Disc Rheometer at 160° C. (320° F.) M_(L) 9.7 M_(H) 40.6 t_(s)2, minutes (Continued) 1.3 t′c(90), minutes 15.8 1.25 * t′c(90), minutes 19.8 Cure Rate Index 6.9 Original Physical Properties Stress @ 100% Elongation, MPa 5.2 psi 760 Stress @ 200% Elongation, MPa 9.5 Stress @ 300% Elongation, MPa — Tensile Ultimate, MPa 11.5 psi 1665 Elongation @ Break, % 260 Hardness Duro A, pts. 78 Specific Gravity 1.329 Yarn Adhesion-CPH Method EMULSION TREATED ARAMID 1008 Average Adhesion Force, lbf/in. width 7.67 std. dev 1.16 SOLUTION TREATED ARAMID 1008 Average Adhesion Force, lbf/in. width 8.34 std. dev 1.51 UNTREATED TWARON ARAMID 1008 Average Adhesion Force, lbf/in. width 5.23 std. dev 0.83 BEAVERLOC 102 TWARON ARAMID Average Adhesion Force, lbf/in. width 10.64 std. dev 0.75 Weight Retention After 30 hrs. @ 65° C. SOLUTION Weight Retention, grams 1.45 Weight Retention, % 48.70 EMULSION Weight Retention, grams 1.48 Weight Retention, % 49.70

[0180] The following Table XVI is a summary of the solvent solubilities of the melamine (Resimene 3520) and RX-1 3804 (di-2-ethylhexyl dimerate) for use in selecting solvents capable of solubilizing both the ester and the resin in making a liquid solution of the adhesion promoter. The solubilities were only determined at 1:1 mixtures of solvent to dimerate/melamine. If both the samples were soluble in the solvent, the solutions were again mixed at a 1:1 ratio of dimerate+solvent to Melamine+solvent. The samples provide complete solubility of both dimerate ester and Melamine resin so long as the composition is at a 13% by weight or greater percent solvent level. TABLE V Melamine/Dimerate Solubilities Spot Checks RX13804 + Solvent RX13804 Melamine Melamine Xylene S S S 1,4-Dioxane S S S Toluene S S S Acetonitrile I S I Ethanol I S I n-Hexanol S S S Ethyl Acetate S S S N,N-Dimethylformamide I S I n-Butanol S S S 2-EH (2-ethylhexanol) S S S Methyl Ethyl Ketone S S S Methyl Isobutyl Ketone S S S Butyl Acetate S S S Chloroform S S S Carbon Tetrachloride S S S Hexane S I I Heptane S I I Isopropanol S S S Isodecyl alcohol S S S Isotridecyl alcohol S S S Ethylene glycol monobutyl S S S ether Dipropylene glycol monobutyl S S S ether Melamine/Dimerate Solubilities with 2-EH Quantitative % Sample % RX13804 Melamine % 2-EH Appearance 1 42.5 42.5 15.0 Clear 2 43.0 43.0 14.0 Clear 3 43.2 43.2 13.6 Clear 4 43.3 43.3 13.4 Clear 5 43.5 43.5 13.0 Hazy (Insoluble)

[0181] In order to homogeneously emulsify the ester and/or the resin components of the adhesion promoter in a water-based carrier, any suitable emulsifying/dispersing agents can be used that are capable of forming a stable emulsion. Since the esters have a very low polarity and the resins have a very high polarity, if both the ester and resin are emulsified in a water-based carrier, generally a combination of emulsifying agents is needed to provide a homogeneous, stable emulsion in water. It has been found that the water-based emulsions should have a hydrophile/lipophile balance (HLB) in the range of about 4 to about 5 for best emulsification. Particular combinations of emulsifying agents found to be especially effective in providing a homogeneous, stable water-based emulsion of the dimerate esters and adhesive resin include a combination of an anionic metal stearate, e.g., potassium stearate for the ester, and a non-ionic sorbitan oleate for the adhesive resin, as shown in the following emulsion preparation guide: RX-13804 49 Stearic acid  0.2 {close oversize brace} K Stearate KOH (45%)  0.1 Cyrez CRA-138M 48.7 Span80 (sorbitan oleate) (2 to 6%) based on the weight of dimerate ester (RX-13804)

[0182] After adding Stearic acid, heat up to 90° C.; add KOH slowly while mixing, mix for 5 minutes, then cool the mixture down to around 50° C. Then add Cyrez, then Span80.

[0183] In accordance with the present invention, it has been found that the addition of one or more reactive organic solvents (diluents) to the rubber compositions described herein, in addition to a solvent used to solubilize the adhesive resin, or as a replacement for any portion, or all of, the resin solvent, unexpectedly increases the adhesion of the rubber composition to substrates such as polymeric cord, metal cord, polymeric fabric, and metal, particularly cords in the manufacture of cord-reinforced rubber articles, such as tires, hoses, conveyor belts, transmission belts, and the like.

[0184] Examples of the reactive diluents include (1) glycidyl ethers, (2) diglycidyl ethers; (3) aliphatic, straight chain epoxides; (4) epoxidized vegetable oils, particularly epoxidized soybean oil; (5) cycloaliphatic epoxies; (6) glycidyl esters, and (7) diglycidyl esters.

[0185] (1) Glycidyl ethers generally have a structural formula as follows:

[0186] where R=alkyl (methyl, ethyl, butyl, isobutyl, and the like), alkyl containing one or more olefinic bonds, or aryl (phenyl, toluyl, benzyl, and the like) these are reaction products of epichlorohydrin with methanol, ethanol, isopropanol, n-butanol, 1-octanol, 2-ethylhexanol, n-decanol, isooctanol, isodecanol, oleyl alcohol, benzyl alcohol, or any other alcohol, as well as mixtures of alcohols, for example, a mixture of n-octyl and n-decyl.)

[0187] Examples include 2-ethylhexyl glycidyl ether; allyl glycidyl ether; dodecyl glycidyl ether; decyl glycidyl ether; iso-butyl glycidyl ether; n-butyl glycidyl ether; naphthyl glycidyl ether; tridecyl glycidyl ether; phenyl glycidyl either; 2-ethylhexyl glycidyl ether; C8-C10 aliphatic glycidyl ether; P-tertiary butyl phenyl glycidyl ether; nonyl phenyl glycidyl either; and phenyl glycidyl ether;

[0188] (2) Diglycidyl ethers generally have a structural formula as follows:

[0189] Where R=a straight chain or branched aliphatic moiety, for example (CH₂)_(n), where n=2-10, or —CH₂—CH(CH₃)CH₂— or —CH₂—C(CH₃)₂—CH₂—, or the like. These are reaction products of epichlorohydrin with a diol or mixtures of diols, such as ethylene glycol, propylene glycol, 1,4-butylene glycol, 1,3-butylene glycol, 1,6-hexanediol, 2-methyl-1,3-propanediol, 2,2-dimethyl-1,3-propanediol, or mixtures. R can also be an aromatic moiety, resulting in an epoxy structure that is the reaction product of glycidol with common bisphenols such as bisphenol A and bisphenol F.

[0190] Examples include 1,6-hexanedioldiglycidyl ether; bisphenol A diglycidyl ether; neopentyl glycol diglycidyl ether; 1,4 butanediol diglycidyl either; cyclohexanedimethanol diglydidyl ether; polypropylene glycol diglycidyl ether; polyethylene glycol diglycidyl ether; dibromo neopentyl glycol diglycidyl ether; trimethylopropane triglycidyl ether; castor oil triglycidyl ether; propoxylated glycerin triglycidyl ether; and sorbitol polyclycidyl either.

[0191] (3) Aliphatic, straight chain epoxides have a general structural formula as follows:

[0192] Examples include propylene oxide, butylene oxide, as well as the following: R₁ R₂ R₃ R₄ CH₂══CH H H H C₃H₇ H H H (CH₃)₂CH H H H C₅H₁₁ H H H C₆H1₃ H H H (CH₃)₂CH(CH₂)₃ H H H C₈H₁₇ H H H C₁₆H₃₃ H H H C₁₈H₃₇ H H H C₆H₅ H H H C₆H₅CH₂ H H H C₆H₅(CH₂)₂ H H H C₆H₅(CH₂)₃ H H H C₅H₅(CH₂)₄ H H H CH₂OH H H H CH₃OCH₂ H H H C₂H₅OCH₂ H H H C₃H₇CHOH H H H C₆H₅OCH₂ H H H CH₃CO₂CH₂ H H H CH₂══CHCO₂CH₂ H H H CH₂══C(CH₃)—CO₂CH₂ H H H CH₃CH══CH—CO₂CH₇ H H H Br H H H CH₂F H H H CH₂Cl H H H CH₂Br H H H CH₂I H H H CF₃ H H H CCl₃ H H H (C₂H₅)₂NCH₂ H H H C₂H₅ H C₂H₅ H C₂H₅ H CF₃ H C₂H₅ H C₃F₇ H C₄H₉ H CH₂Br H C₅H₁₁ H Cl H C₆H₅ H CH₃ H C₆H₅ H C₂H₅ H C₆H₅ H C₃H₇ H C₆H₅ H C₃H₇ (iso) H C₆H₅ H C₆H₅CH₂ H CF₃ H F H CH₃ CH₃ CH₃ H CH₃ C₂H₅ CH₃ H CH₃ CH₃ C₃F₇ H CH₃ CH₃ CO₂C₂H₅ H CH₃ CF₃ Cl H C₂H₅ C₂H₅ OH₃ H CH₃ CH₃ CH₃ CH₃ CH₃ CH₃ H H CH₃ CF₃ H H CH₃ C₂H₅ H H CH₃ C₃F₇ H H C₂H₅ CH₂Br H H C₆H₅ CH₃ H H C₆H₅(CH₂)₃ CH₃ H H C₆H₅ OH H H Cl Cl H H CH₃ H CH₃(cis) H CH₃ H H CH₃(trans) CH₃ H C₂H₅(cis) H CH₃ H H C₂H₆(trans) CH₃ H C₃H₇ H CH₃ H C₃H₇(iso) H CH₃ H CF₃ H CH₃ H CH₂Br H CH₃ H C₃F₇ H CH₃ H CO₂H H

[0193] (4) Epoxidized oils such as epoxidized soybean oil, epoxidized linseed oil, epoxidized safflower oil, epoxidized corn oil, epoxidized cottonseed oil, epoxidized rapeseed oil, epoxidized peanut oil, and other similar species derived from epoxidation of C₁₈ unsaturated esters of glycerin.

[0194] (5) Cycloaliphatic epoxies, such 1,2-cyclohexene oxide, 1,2-cyclopentene oxide, 1,2,3,4,-diepoxybutene, vinylcyclohexene dioxide, and the like, as well as those products marketed by Shell Oil under the brand name EPON®, an example of which is shown below.

[0195] (6) Glycidyl esters generally have a structural formula as follows:

[0196] Where R=straight chain aliphatic, such as —(CH₂)_(n)—CH₃ (n=1-9) or branched aliphatic such as —CH₂CH(CH₃)₂ and —CH(CH₂CH₃)(CH₂)₄CH₃. R can also be straight chain aliphatic, containing one or more olefinic bonds. R can also be aromatic, i.e., -phenyl or -toluyl. These glycidyl esters are reaction products of glycidol with carboxylic acids, such as acetic acid, propionic acid, isobutyric acid, 2-ethylhexoic acid, benzoic acid, toluic acid (various isomers), oleic acid, linoleic acid, linolenic acid, as well as mixtures of carboxylic acids.

[0197] Examples include glycidyl neodecanoate; acetic acid glycidyl ester; butyric acid glycidyl ester; propionic acid glycidyl ester; valeric acid glycidyl ester; caproic acid glycidyl ester; capric acid glycidyl ester; caprylic acid glycidyl ester; lauric acid glycidyl ester; and glycidyl ester of linoleic acid or of linolenic acid.

[0198] (7) Diglycidyl esters generally have a structural formula as follows:

[0199] Where R=straight chain aliphatic, —(CH₂)_(n) (n=1-8) or branched aliphatic, or aliphatic/cycloaliphatic mixed, or aliphatic containing one or more olefinic bonds. R can also be aromatic. These diglycidyl esters are reaction products of glycidol with dicarboxylic acids such as malonic acid, glutaric acid, adipic acid, azelaic acid, sebacic acid, phthalic anhydride, isophthalic acid, terephthalic acid, and one or more dimer acids. Water-Based Emulsion Adhesion Promoter RX-13937 Composition Component % by wt. Chemical Supplier RX-13804 49.0 Di-2-ethylhexyl dimerate CP Hall Stearic acid 0.2 tripled pressed Stearic acid Witco KOH (45%) 0.1 Potassium hydroxide 45% Ashta Cyrez CRA-138M 48.7 methylated melamine, Cytec formaldehyde polymer Span80 2.0 sorbitan monooleate Uniqema

[0200] Solution-Based Adhesion Promoter RX-13928 Composition Component % by wt. Chemical Supplier ester 42.5 Di-2-ethylhexyl dimerate CP Hall resin 42.5 methylated melamine UCB formaldehyde resin solvent 15.0 2-ethylhexanol Sunoco 

What is claimed is:
 1. A vulcanized rubber composition comprising rubber selected from the group consisting of natural rubber, synthetic rubber, and a combination thereof; and a liquid adhesion promoter selected from the group consisting of a solution and a water-based emulsion containing (1) an adhesive resin in an amount of about 0.1% to about 15% by weight, based on the weight of rubber in the composition; (2) a vulcanizing agent for the rubber in an amount sufficient to vulcanize said rubber; (3) a reactive diluent in an amount of about 0.5% to about 50% by weight, based on the total weight of the adhesive resin plus ester of formula I-IV; and (4) an ester having formula I, II, III, IV or a combination of any two or more of said esters in an amount of about 0.1% to about 15% by weight, based on the weight of rubber in the composition:

wherein R¹ is a C₃-C₂₄ alkyl radical, straight chain or branched, saturated, or unsaturated containing 1 to 3 carbon-to-carbon double bonds; R² is a C₃-C₂₄ saturated fatty acid residue, or an unsaturated fatty acid residue having 1 to 6 carbon-to-carbon double bonds;

wherein n=3-24, and R³ and R⁴, same or different, are a C₃-C₂₄ alkyl radical, straight chain or branched, saturated, or unsaturated containing 1 to 3 carbon-to-carbon double bonds;

wherein R⁵ and R⁷, same or different, are a C₃-C₂₄ hydrocarbon chain, straight chain or branched, either saturated or having 1 to 6 carbon-to-carbon double bonds; R⁶ and R⁸, same or different, are C₃-C₂₄ alkyl radical, straight chain or branched, saturated, or unsaturated containing 1 to 3 carbon-to-carbon double bonds; and R¹⁰ and R¹¹, same or different, are a C₃-C₂₄, saturated hydrocarbon chain, straight chain or branched; or an unsaturated C₃-C₂₄, hydrocarbon chain, straight chain or branched, having 1 to 6, carbon-to-carbon double bonds;

wherein R¹², R¹⁴ and R¹⁸, same or different, are a C₃-C₂₄, hydrocarbon chain, straight chain or branched, either saturated or having 1 to 6 carbon-to-carbon double bonds; R¹³, R¹⁵ and R¹⁹, same or different, are a C₃-C₂₄ alkyl radical, straight chain or branched, saturated, or unsaturated containing 1 to 3 carbon-to-carbon double bonds; and R¹⁶, R¹⁷ and R²⁰, same or different, are a C₃-C₂₄ saturated hydrocarbon chain, straight chain or branched; or unsaturated C₃-C₂₄ hydrocarbon chain, straight chain or branched, containing 1 to 6 carbon-to-carbon double bonds.
 2. The rubber composition in accordance with claim 1, wherein the ester is selected from the group consisting of formula I, II, III, IV, and a combination of any two or more of said esters:

wherein R¹ is a C₃-C₁₈ alkyl radical, straight chain or branched, saturated, or unsaturated containing 1 to 3 carbon-to-carbon double bonds; and R² is a C₈-C₁₈ saturated fatty acid residue, or an unsaturated fatty acid residue having 1 to 3 carbon-to-carbon double bonds;

wherein n=6-18, and R³ and R⁴, same or different, are a C₃-C₁₈ alkyl radical, straight chain or branched, saturated, or unsaturated containing 1 to 3 carbon-to-carbon double bonds;

wherein R⁵ and R⁷, are a C₆-C₂₄ hydrocarbon chain, straight chain or branched; either saturated or having 1 to 3 carbon-to-carbon double bonds; R⁶ and R⁸, same or different, are a C₃-C₁₈ alkyl radical, straight chain or branched, saturated, or unsaturated containing 1 to 3 carbon-to-carbon double bonds; and R¹⁰ and R¹¹, same or different, are a C₃-C₁₈, saturated hydrocarbon chain, straight chain or branched; or an unsaturated hydrocarbon chain, straight chain or branched, containing 1 to 3 carbon-to-carbon double bonds;

wherein R¹², R¹⁴ and R¹⁸, same or different, are a C₈-C₁₈, hydrocarbon chain, straight chain or branched, either saturated or having 1 to 3 carbon-to-carbon double bonds; R¹³, R¹⁵ and R¹⁹, same or different, are a C₆-C₁₈ alkyl radical, straight chain or branched, saturated, or unsaturated containing 1 to 3 carbon-to-carbon double bonds; and R¹⁶, R¹⁷ and R²⁰, same or different, are a C₆-C₁₈ saturated hydrocarbon chain, straight chain or branched; or an unsaturated C₆-C₁₈ hydrocarbon-chain, straight chain or branched, containing 1 to 3 carbon-to-carbon double bonds; and wherein said reactive diluent is a monomer selected from the group consisting of (1) a glycidyl ether; (2) a diglycidyl ether; (3) an aliphatic, straight chain epoxide; (4) an epoxidized vegetable oil; (5) a cycloaliphatic epoxy; (6) a glycidyl ester; (7) a diglycidyl ester; and any combination thereof, present in the composition in an amount of about 5% to about 40% by weight, based on the total weight of adhesive resin plus ester of formula I-IV.
 3. The rubber composition of claim 1, wherein the adhesive resin is a condensation product of a methylene acceptor and a methylene donor.
 4. The rubber composition in accordance with claim 3, wherein the adhesive resin is selected from the group consisting of phenol-formaldehyde, melamine-formaldehyde; naphthol-formaldehyde; polyepoxide; a reaction product of triallyl cyanurate, resorcinol, and formaldehyde; a reaction product of p-chlorophenol, resorcinol, and formaldehyde; a copolymer of styrene, butadiene, and 2-vinylpyridine; and mixtures thereof.
 5. The rubber composition in accordance with claim 4, wherein the phenol-formaldehyde resin is resorcinol-formaldehyde.
 6. The rubber composition in accordance with claim 1, wherein the adhesive resin is selected from the group consisting of derivatives of melamine, acetoguanamine, benzoguanamine, cyclohexylguanamine and glycoluril monomers and oligomers of these monomers, which have been substituted on average at two or more positions on the monomer or on each unit of the oligomer with vinyl terminated radicals, the rubber composition being free of resorcinol.
 7. The rubber composition in accordance with claim 6, wherein at least one of the adhesive resins has been further substituted on average at one or more positions with a, radical which comprises carbamoylmethyl or amidomethyl.
 8. The rubber composition in accordance with claim 6, wherein the adhesive resin is selected from compounds of the formula:

and positional isomers thereof, wherein, in each monomer and in each polymerized unit of the oligomers, Y is selected from methyl, phenyl and cyclohexyl, and, on average, at least two R are —CH₂—R¹, and any remaining R are H, and at least 2 R¹ are radicals selected from CH₂═C(R²)—C(O)O—, CH₂═C(R²)—C(O)-Z, CH₂═C(R²)C(O)—NH—, and CH₂═C(R²)—CH₂—O—, wherein R² is hydrogen or C₁-C₁₈ alkyl, and Z is a radical selected from —O—CH₂—CH₂—O—, —O—CH₂—CH(CH₃)—O—, —O—CH₂—CH₂—CH₂O—, and —O—CH(C₂H₅)—O—, and any remaining R¹ radicals are selected from —O—R³, —NH—C(O)—OR⁴, and —NH—C(O)—R⁴, and wherein R₃ is hydrogen or R₄, and R₄ is a C₁-C₁₈ alkyl, alicyclic, hydroxyalkyl, alkoxyalkyl or aromatic radical, and in the oligomers, P is 2 to about 10, and L is methylene or the radical —CH₂—O—CH₂—.
 9. The rubber composition in accordance with claim 8, wherein on average at least one R¹ in each monomer or in each oligomerized unit of the adhesive resin is: —NH—C(O)—OR⁴ wherein R⁴ is as defined in claim
 8. 10. The rubber composition in accordance with claim 9, wherein the adhesive resin is a compound of the formula

wherein P is 2 to about 10, L is methylene or the radical —CH₂—O—CH₂—, and R is as follows: at least two R are —CH₂—R¹, and any remaining R are H, and at least 2 R¹ are radicals selected from CH₂═C(R²)—C(O)—O—, CH₂═C(O)—Z, CH₂═C(R²)—C(O)NH—, and CH₂═C(R²)—CH₂—, wherein R² is hydrogen or C₁-C₁₈ alkyl, and Z is a radical selected from —O—CH₂—CH₂—O—, —O—CH₂—CH(CH₃)—O—, —O—CH₂—CH₂—CH₂O—, and —O—CH(C₂H₅)—O—, and any remaining R¹ radicals are selected from —O—R³, —NH—C(O)—OR⁴, and —NH—C(O)—R⁴, and wherein R₃ is hydrogen or R₄, and R₄ is a C₁-C₁₈ alkyl, alicyclic, hydroxyalkyl, alkoxyalkyl or aromatic radical.
 11. The rubber composition in accordance with claim 10, wherein in the adhesive resin formulas, on average at least one R radical in each monomer or in each oligomerized unit is —CH₂—NH—C(O)—OR⁴ wherein R⁴ is a C₁-C₁₈ alkyl, alicyclic, hydroxyalkyl, alkoxyalkyl or aromatic radical.
 12. The rubber composition in accordance with claim 10, wherein on average at least two R radicals are selected from CH₂═C(CH₃)—C(O)O—C₃H₆—CH₂—and CH₂═CH₂—C(O)O—C₂H₄—O—CH₂— and at least one R radical is selected from CH₂—NH—C(O)—O—CH_(3 and) CH₂—NH—C(O)—O—C₃H₇.
 13. The rubber composition in accordance with claim 8, further comprising an additional additive selected from hydroxymethylated and alkoxymethylated (alkoxy having 1-5 carbon atoms) derivatives of melamine, acetoguanamine, benzoguanamine, cyclohexylguanamine and glycoluril and their oligomers.
 14. The rubber composition in accordance with claim 6, wherein the adhesive resin is a derivative of melamine or an oligomer of melamine.
 15. The rubber composition in accordance with claim 6, wherein the adhesive resin is a derivative of acetoguanamine or an oligomer of acetoguanamine.
 16. The rubber composition in accordance with claim 6, wherein the adhesive resin is a derivative of benzoguanamine or an oligomer of benzoguanamine.
 17. The rubber composition in accordance with claim 6, wherein the adhesive resin is a derivative of cyclohexylguanamine or an oligomer of cyclohexylguanamine.
 18. The rubber composition in accordance with claim 1, wherein the adhesive resin is a self-condensing alkylated triazine resin selected from the group consisting of (i), (ii), and (iii): (i) a self-condensing alkylated triazine resin having at least one of imino or methylol functionality and represented by formula (I)

(ii) an oligomer of (i), or (iii) a mixture of (i) and (ii), wherein Z is —N(R)(CH₂OR¹), aryl having 6 to 10 carbon atoms, alkyl having 1 to 20 carbon atoms or an acetyl group, each R is independently hydrogen or —CH₂OR¹, and each R¹ is independently hydrogen or an alkyl group having 1 to 12 carbon atoms, provided that at least one R is hydrogen or —CH₂OH and at least one R¹ is selected from the alkyl group; and wherein the rubber composition is substantially free of methylene acceptor coreactants.
 19. The rubber composition in accordance with claim 18, wherein at least one R group of the alkylated triazone resin is hydrogen.
 20. The rubber composition in accordance with claim 19, wherein at least one R¹ group of the alkylated triazone resin is a lower alkyl group having 1 to 6 carbon atoms.
 21. The rubber composition in accordance with claim 20, wherein the adhesive resin is a derivative of melamine, benzoguanamine, cyclohexylguanamine, or acetoguanamine, or an oligomer thereof.
 22. The rubber composition in accordance with claim 20, wherein Z is —N(R)(CH₂OR¹).
 23. The rubber composition in accordance with claim 4, wherein the phenol-formaldehyde resin is resorcinol-formaldehyde; and the melamine-formaldehyde resin is N-(substituted oxymethyl) melamine-formaldehyde.
 24. The rubber composition in accordance with claim 1, wherein the ester has the formula II and comprises a saturated diester formed by the reaction of sebacic acid and a C₆-C₂₄ alcohol, straight chain or branched, saturated, or unsaturated containing 1 to 3 carbon-to-carbon double bonds.
 25. The rubber composition in accordance with claim 24, wherein the alcohol is 2-ethylhexyl alcohol, and the ester has the following formula:


26. The rubber composition in accordance with claim 1, wherein the ester is an unsaturated diester formed by the reaction of a C₃₆ dimer acid and a C₃-C₁₈ alcohol, straight chain or branched, saturated, or unsaturated containing 1 to 3 carbon-to-carbon double bonds.
 27. The rubber composition in accordance with claim 26, wherein the alcohol is 2-ethylhexyl alcohol.
 28. The rubber composition in accordance with claim 26, wherein the alcohol is tridecyl alcohol.
 29. The rubber composition in accordance with claim 26, wherein the alcohol is oleyl alcohol.
 30. The rubber composition in accordance with claim 1, wherein the ester comprises the following dimer acid reacted with a C₃-C₂₄ alcohol:


31. The rubber composition in accordance with claim 1, wherein the ester comprises the following dimer acid reacted with a C₃-C₂₄ alcohol:


32. The rubber composition in accordance with claim 1, wherein the ester comprises the following dimer acid reacted with a C₃-C₂₄ alcohol:


33. The rubber composition in accordance with claim 1, wherein the ester is the reaction product of a C₃-C₂₄ alcohol with a tricarboxylic acid, having the following formula:


34. The rubber composition in accordance with claim 1, wherein the ester is a combination of compounds of formula I, II, III, and IV.
 35. The rubber composition in accordance with claim 34, wherein the ester is a reaction product of a C₃-C₂₄ alcohol straight chain or branched, saturated, or unsaturated having 1 to 3 carbon-to-carbon double bonds, with a dimer acid having CAS #61788-89-4.
 36. The rubber composition in accordance with claim 35, wherein the alcohol is 2-ethylhexyl alcohol.
 37. The rubber composition in accordance with claim 35, wherein the alcohol is a tridecyl alcohol.
 38. The rubber composition in accordance with claim 35, wherein the alcohol is an oleyl alcohol.
 39. The rubber composition in accordance with claim 1, wherein the R², R⁵, R⁷, R¹², R¹⁴ are fatty acid residues derived from animal or vegetable fatty acids.
 40. The rubber composition of claim 39, wherein the fatty acids are selected from the group consisting of butter; lard; tallow; grease; herring; menhaden; pilchard; sardine; babassu; castor; coconut; corn; cottonseed; jojoba; linseed; oiticia; olive; palm; palm kernel; peanut; rapeseed; safflower; soya; sunflower; tall; tung; and mixtures thereof.
 41. The rubber composition of claim 40, wherein the fatty acid residues are selected from the group consisting of hexanoic; octanoic; decanoic; dodecanoic; 9-dodecenoic; tetradecanoic; 9-tetradecenoic; hexadecanoic; 9-hexadecenoic; octadecanoic; 9-octadecenoic; 9-octadecenoic, 12-hydroxy; 9,12-octadecadienoic; 9,12,15-octadecatrienoic; 9,11,13-octadecatrienoic; 9,11,13-octadecatrienoic, 4-oxo; octadecatetrenoic; eicosanoic; 11-eicosenoic; eicosadienoic; eicosatrienoic; 5,8,11,14-eicosatetraenoic; eicosapentaenoic; docosanoic; 13-docosenoic; docosatetraenoic; 4,8,12,15,19-docosapentaenoic; docosahexaenoic; tetracosenoic; and 4,8,12,15,18,21-tetracosahexaenoic.
 42. A method of increasing the adhesion of a rubber composition to a substrate, said rubber composition including a natural or synthetic rubber; a vulcanizing agent for said rubber; and an adhesive resin, comprising adding a reactive diluent to said rubber composition, in an amount of about 0.5% to about 50% by weight, based on the total weight of the adhesive resin plus ester of formula I-IV, and about 0.1% to about 15% by weight, based on the weight of the rubber, of a liquid ester additive of formula I, II, III, IV, or mixtures thereof:

wherein R¹ is a C₃-C₂₄ alkyl radical, straight chain or branched, saturated, or unsaturated containing 1 to 3 carbon-to-carbon double bonds; R² is a C₃-C₂₄ saturated fatty acid residue, or an unsaturated fatty acid residue having 1 to 6 carbon-to-carbon double bonds;

wherein n=3-24 and R³ and R⁴, same or different, are a C₃-C₂₄ alkyl radical, straight chain or branched;

wherein R⁵ and R⁷, same or different, are a C₃-C₂₄ hydro carbon chain, straight chain or branched, either saturated or having 1 to 6 carbon-to-carbon double bonds; R⁶ and R⁸, same or different, are a C₃-C₂₄ alkyl radical, straight chain or branched; and R¹⁰ and R¹¹, same or different, are a C₃-C₂₄, saturated hydrocarbon chain, straight chain or branched; or an unsaturated C₃-C₂₄, hydrocarbon chain, straight chain or branched, having 1 to 6 carbon-to-carbon double bonds;

wherein R², R¹⁴ and R¹⁵, same or different, are a C₃-C₂₄ hydrocarbon chain, straight chain or branched, either saturated or having 1 to 6 carbon-to-carbon double bonds; R¹³, R¹⁵ and R¹⁹, same or different, are C₃-C₂₄ alkyl radical, straight chain or branched, saturated, or unsaturated containing 1 to 3 carbon-to-carbon double bonds; and R¹⁶, R¹⁷ and R²⁰, same or different, are C₃-C₂₄ saturated hydrocarbon chain, straight chain or branched; or unsaturated C₃-C₂₄ hydrocarbon chain, straight chain or branched, containing 1 to 6 carbon-to-carbon double bonds; and comprising subjecting the composition to conditions sufficient to vulcanize the rubber in said composition, such that the reactive diluent strengthens the adherence between the rubber and the substrate.
 43. The method in accordance with claim 42, wherein the substrate is a plurality of cords, and the reactive diluent is a monomer selected from the group consisting of (1) a glycidyl ether; (2) a diglycidyl ether; (3) an aliphatic, straight chain epoxide; (4) an epoxidized vegetable oil; (5) a cycloaliphatic epoxy; (6) a glycidyl ester; (7) a diglycidyl ester; and any combination thereof, present in the composition in an amount of about 5% to about 40% by weight, based on the total weight of adhesive resin plus ester of formula I-IV.
 44. The method in accordance with claim 42, wherein the substrate is a polymeric sheet or fabric, and the reactive diluent is a monomer selected from the group consisting of (1) a glycidyl ether; (2) a diglycidyl ether; (3) an aliphatic, straight chain epoxide; (4) an epoxidized vegetable oil; (5) a cycloaliphatic epoxy; (6) a glycidyl ester; (7) a diglycidyl ester; and any combination thereof, present in the composition in an amount of about 5% to about 40% by weight, based on the total weight of adhesive resin plus ester of formula I-IV.
 45. The method in accordance with claim 42, wherein the substrate is flat metal stock material, and the reactive diluent is a monomer selected from the group consisting of (1) a glycidyl ether; (2) a diglycidyl ether; (3) an aliphatic, straight chain epoxide; (4) an epoxidized vegetable oil; (5) a cycloaliphatic epoxy; (6) a glycidyl ester; (7) a diglycidyl ester; and any combination thereof, present in the composition in an amount of about 5% to about 40% by weight, based on the total weight of adhesive resin plus ester of formula I-IV.
 46. A method of increasing the adhesion of a rubber composition, containing a vulcanizing agent for the rubber, to a substrate comprising an expedient selected from the group consisting of (1) applying a liquid adhesion promoter comprising an adhesive resin component, a reactive diluent component, and an ester component to the substrate prior to contacting the substrate with the rubber composition; (2) contacting the substrate separately with a solvent solution containing a reactive diluent or water-based emulsion containing the ester component and the reactive diluent component of the liquid adhesion promoter, and contacting the substrate separately with a solvent solution containing a reactive diluent, or water-based emulsion containing the adhesive resin component and the reactive diluent component of the liquid adhesion promoter prior to contacting the substrate with the rubber composition; (3) applying the adhesive resin component and the reactive diluent component of the liquid adhesion promoter to the substrate prior to contacting the adhesive resin-applied substrate with the rubber composition containing a solvent solution or water-based emulsion containing the ester component of the liquid adhesion promoter; (4) applying the ester component of the liquid adhesion promoter to the substrate prior to contacting the ester-applied substrate with the rubber composition containing a solvent solution or water-based emulsion containing the adhesive resin component and the reactive diluent component of the liquid adhesion promoter; wherein the ester component of the adhesion promoter is selected from the group consisting of formulas I, II, III, IV, and a combination of any two or more:

wherein R¹ is a C₃-C₂₄ alkyl radical, straight chain or branched, saturated, or unsaturated containing 1 to 3 carbon-to-carbon double bonds; R² is a C₃-C₂₄ saturated fatty acid residue, or an unsaturated fatty acid residue having 1 to 6 carbon-to-carbon double bonds;

wherein n=3-24, and R³ and R⁴, same or different, are a C₃-C₂₄ alkyl radical, straight chain or branched, saturated, or unsaturated containing 1 to 3 carbon-to-carbon double bonds;

wherein R⁵ and R⁷, same or different, are a C₃-C₂₄ hydrocarbon chain, straight chain or branched, either saturated or having 1 to 6 carbon-to-carbon double bonds; R⁶ and R⁸, same or different, are C₃-C₂₄ alkyl radical, straight chain or branched, saturated, or unsaturated containing 1 to 3 carbon-to-carbon double bonds; and R¹⁰ and R¹¹, same or different, are a C₃-C₂₄, saturated hydrocarbon chain, straight chain or branched; or an unsaturated C₃-C₂₄, hydrocarbon chain, straight chain or branched, having 1 to 6, carbon-to-carbon double bonds;

wherein R¹², R¹⁴ and R¹⁸, same or different, are a C₃-C₂₄, hydrocarbon chain, straight chain or branched, either saturated or having 1 to 6 carbon-to-carbon double bonds; R¹³, R¹⁵ and R¹⁹, same or different, are a C₃-C₂₄ alkyl radical, straight chain or branched, saturated, or unsaturated containing 1 to 3 carbon-to-carbon double bonds; and R¹⁶, R¹⁷ and R²⁰, same or different, are a C₃-C₂₄ saturated hydrocarbon chain, straight chain or branched; or unsaturated C₃-C₂₄ hydrocarbon chain, straight chain or branched, containing 1 to 6 carbon-to-carbon double bonds; and comprising subjecting the composition to conditions sufficient to vulcanize the rubber in said composition, such that the reactive diluent strengthens the adherence between the rubber and the substrate.
 47. The method in accordance with claim 46, wherein the amount of the adhesive resin component contained in the rubber composition or applied to the substrate is about 0.1% to about 15% by weight, based on the weight of rubber in the composition, the amount of ester component contained in the rubber composition or applied to the substrate is about 0.1% to about 15% by weight, based on the weight of rubber in the composition, and the amount of the reactive diluent component contained in the rubber composition or applied to the substrate is about 0.5% to about 50% by weight, based on the total weight of the adhesive resin component plus ester component.
 48. A cord-reinforced article of manufacture comprising a plurality of cords selected from polymeric cords, metal cords, glass cords, and a combination thereof, adhered to the rubber composition of claim
 1. 